2010 年第7 期 福　　建　　建　　筑 No7 ·2010 总第 145期 Fujian Architecture Construction Vol ·145 焊接残余应力对焊接结构的影响 1 2 葛明兰 　鲁家晟 (1.西安欧亚学院　710065;2. 西建工集团第一建筑工程有限公司　710068) 摘　要:焊接残余应力是焊件产生变形和开裂等缺陷的主要原因, 由于其影响因素众多, 本文分别从焊接残余应力对结构的刚度、 受压杆件稳定性、静载强度、疲劳强度、构件脆性、焊件加工精度和尺寸稳定性等方面进行分析研究残余应力对焊接结构产生的影 响。 关键词:焊接残余应力　刚度　强度　受压构件稳定性 中图分类号:TU3　　　　　　文献标识码:B　　　　　　文章编号:1004-6135(2010)07-0050-03 The Influence Of Welding residual StressTo Welded Steel Structure 1 2 Ge inglan 　Lu Jiasheng (1.Xian Eurasia University　710065;2.The Firstt Engineering Limited Of Shaanxi Construction Engineering Group　710068) Abstract:Welding residual stress is welded defects such as distortion and cracking of the main reasons, because of its large num- ber of factors, Analysis of the welding residual stress on the stiffness of the structure, by the bar piece stability, static strength, fatigue, brittle components, weldment machining accuracy and dimensional stability analysis in areas such as welding residual stress on the impact of the structure. Welding residual stress　Stiffness　Strength　Stability of compression members Keywords: 0　引言 焊接构件由焊接而产生的内应力称之为焊接应力, 按作用 时间可分为焊接瞬时应力和焊接残余应力。焊接过程中, 某一 瞬时的焊接应力称之为焊接瞬时应力, 它随着时间而变化。焊 后残留在焊件内的焊接应力称之为焊接残余应力。 对于钢结 构而言, 焊接残余应力和变形是影响结构断裂强度、疲劳强度 和结构稳定性的重要因素。焊接残余应力大大降低了焊接部 [1] 位材料的有效比例极限, 是结构发生脆断的主要原因之一 。 (a) (b) (c) 焊接结构中, 残余拉应力还会降低结构抗疲劳和耐腐蚀的能 (a)、(b)施焊时焊缝及附近温度场　(c)钢板生的纵向焊接残余应力 力;残余压应力会降低受压构件的刚度, 从而使稳定承载力。 图1　施焊时焊缝及附近温度场和焊接残余应力 焊接残余应力是焊件产生