鞍钢鲅鱼圈钢厂钢渣短流程处理及应用实践.pdfVIP

鞍钢鲅鱼圈钢厂钢渣短流程处理的应用与实践 苏兴文 李晓阳 刘 镭 （鞍钢矿渣开发公司，鞍山 114021 ） 1 摘 要 鞍钢集团鲅鱼圈钢铁厂炼钢产生的钢渣采用国内最先进的短流程处理工艺进行处理。其中钢渣热闷生产线 为国内第一条熔融态钢渣热闷加工线，将 1400℃熔融钢直接倒入热闷池进行打水热闷解决了钢渣利用中的膨胀问 题，使钢渣可以得到充分利用。钢渣磁选生产线在传统钢渣磁选加工线基础上进行了改良，使金属铁回收率达到 98% 以上，为鞍钢鲅鱼圈钢厂炼钢生产的成本降低作出了重大贡献。 关键词 短流程 钢渣热闷 钢渣磁选 Application and Practice of Short-flow Processing Technology in Bayuquan Iron-steel Company Under AG Su Xingwen Li Xiaoyang Liu Lei （Slag Development Company of Anshan Iron Steel Group Co., Anshan,114021） Abstract Anshan Iron and Steel Group’s steel plant Bayuquan slag produced using the most advanced treatment process for processing short process. One production line of steel slag for domestic hot stuffy first molten steel slag processing line hot stuffy, the 1400 ℃ hot molten steel directly into the pool to fetch water hot stuffy stuffy solve the problem of slag used in the expansion, so that slag can be fully utilized. Steel slag magnetic separator in the traditional production line based on the processing line was modified to make the metal more than 98% iron recovery, the Anshan Iron and Steelmaking Bayuquan reduce the cost of steel has made a significant contribution. Key words short-flow, steel slag hot stifle, steel slag magnetic separation 1 引言 随着鞍钢鲅鱼圈钢厂的建立，为了利用鲅鱼圈钢厂炼钢产生的冶金渣资源，促进鲅鱼圈钢厂可持续发展 和节约型生产，降低钢厂炼钢成本，扩大鞍钢集团公司的多元化发展，鞍钢集团在鲅鱼圈钢厂采用了熔融钢 渣热闷和钢渣棒磨磁选的一整套短流程钢渣处理生产线（见图 1）。经过3 年多的实践，取得了良好的效果。 图 1 鲅鱼圈钢渣处理流程 苏兴文，男，高级工程师，从事冶金渣开发利用。 第八届（2011 ）中国钢铁年会论文集 2 钢渣热闷处理生产线 2.1 钢渣热闷的必要性 钢渣中一般含有 7%～10%的废钢，磁选加工后，可回收其中的90%左右的废钢；除部分废钢外，钢渣 的主要矿物组成为硅酸二钙、硅酸三钙、铁酸钙及RO 相等，与水泥熟料化学成分相似，可作为建材材料。 但目前我国钢尾渣的综合利用率仅达到 10%，其主要原因是钢渣的处理工艺和设备落后，致使钢渣的体积 稳定性不良[1]，用做回填材料、道路材料、水泥和混凝土掺和料、建材制品均会造