3 宝钢不锈钢 2500m 高炉出铁沟热套浇浇注料的研制及应用 陶斯江 张振伟 胡志清 陈曙 （宝钢股份不锈钢事业部炼铁厂，上海 200431 ） 摘 要 研究了 SiC 加入量对出铁沟浇注料性能的影响。以往出铁沟中修时渣、铁线位都采用不同的浇注料，为 了满足性能其中SiC 的加入量各有不同，也给施工以及寿命带来很大的局限性。SiC 加入量越多，浇注料的抗渣性 能越好，但是加入过多的SiC 会导致浇注料气孔率的升高和强度的下降。本次研制发现SiC 含量为18%时，出铁沟 渣、铁线位的侵蚀速率基本达到一致，也为以后的套浇创造条件。 关键词 气孔率 强度 侵蚀速率 铁线 渣线 The Development and Application About the Iron Ditch Hot Set of Castables of 2500m3 Blast Furnace of Stainless Steel Branch of Baosteel Tao Sijiang Zhang Zhenwei Hu Zhiqing Chen Shu (Iron making Plant of Stainless Steel Branch of Baoshan Iron Steel Co., Ltd.,Shanghai,200431) Abstract Studied different SiC addition amount of the iron ditch castable properties. SiC addition amount, the more castable slag performance is better, but joins overmuch two-digit SiC castable porosity can lead to rising and intensity of decline. The research found that SiC content 18%, the iron ditch slag, clematis erosion rate basically reaching a consensus, but also for the set of watering create conditions. Key words porosity, strength, erosion rate, clematis, slag line 1 引言 宝钢不锈钢2500m3 高炉主沟渣、铁线位分别采用了不同的浇注料，渣线位的浇注料SiC 含量较高，铁 线位的浇注料SiC 含量较低。而工作层厚度仅280mm，通过一次中修每轮通铁量在13 万吨左右，下线时都 要将工作层完全拆除。1 根据拆除过程的破损调查情况来看，除局部位置（冲击区渣、铁线过渡区及以上）熔损比较严重外，大 部分耐火材料都有较厚残存，从而造成大量不必要的耐火材料损耗和废弃物污染（每次消耗材料35t ）；另外， 由于多次机械解体，给整体性较差的永久层耐火材料带来很大的冲击损伤，增加维护费用的同时，也埋下后 果严重的安全隐患。由于渣铁线采用两种料，施工过程相对较为复杂，在两种料的交界面容易产生裂纹。 为提高施工的便利性和快捷性，降低耐火材料消耗，提高使用寿命，确保安全受铁，专门研制了一种浇 注料，应用于主沟工作层的渣线及铁线位，按照部分拆除、整体套浇的工艺模式循环使用。由于渣、铁线位 使用环境的差异，不同SiC 含量的浇注料侵蚀速率存在差异，需要该材料在渣、铁线位都保持优异的性能， 才能满足需求。 陶斯江，男，大学本科，助理工程师，从事耐材技术管理，taosijiang@ 8-320 第八届（2011 ）中国钢铁年会论文集 2 实验过程 实验所采用的原料主要有棕刚玉（w(Al O ) ≥96% ）、电熔致密刚玉（w(Al O ) ≥99% ）、氧化铝微粉 2 3