Series No . 3 13 金 　　属 　　矿 　　山 总第 3 13 期 J uly 　2002 　　　　　　　　　　　　　　 M ETAL M IN E 　　　　　　　　　　　　　　2002年第 7 期 不同时效处理对堆焊层的硬度和耐磨性影响 洪永昌 (安徽工业大学) 摘 　要 　研究了2 种不同堆焊材料的堆焊层 ,随不同温度 ,不同时间时效处理的组织和性能变化 ,并采用 SEM 对其磨损表面微观形貌进行了观察和分析 。试验结果表明 ,不同焊材堆焊层 ,焊态时硬度高但耐磨性低 ;堆焊层的 ( ) 焊态与经 560 ℃时效态相比 ,焊态时的耐磨性较差 ;相同时效温度 560 ℃ ,长时时效态硬度比短时时效态低 ,但其 耐磨性优于短时时效态 。 关键词 　时效处理 　堆焊层 　耐磨性 Eff ect of Diff erent Aging Treatment on the Hardness and Wearresistance of Hardfacing Layers Hong Yongchang ( A nhui University of Technology) Abstract 　The structure and p erformance changes of t he hardfacing layers of two different welding materials wit h t he ageing treat ment of different temp eratures and time were studied and t he micromorp hology of t heir wear surface was ab served and analysed by SEM . The result s show t hat t he hardfacing layers of different welding materials , when in welding condition , have a high hardness but low wearresistance . They have an inferior wearresistance in welding condition to t hat in t he condition of ageing at 560 ℃and have a lower hardness but a better wearresistance in t he long time ageing ( ) condition t han t hat in t he short at a similar ageing temp erature 560 ℃ . Keywords 　Ageing treat ment , Hardfacing layer , Hardness , Wearresistance 　　对于冶金 、矿山工业上使用的某些重要零部件 , 2 # ) 。堆焊母材选用尺寸为 500 mm ×300 mm ×20 磨损严重的必须经常更换 ,据有关资料介绍[ 1 ] , 磨 mm 的 Q235 板材作为试板 。 损给工业国家带来的损失可达国民生产总值的 2 % 12