鞍钢鲅鱼圈分公司高炉合理造渣制度与研究.pdfVIP

鞍钢鲅鱼圈分公司高炉合理造渣制度研究 郭天永 车玉满 李春明 孙 鹏 李晓伟 李连成 姚 硕 ( 鞍钢股份有限公司，鞍山 114009 ) 摘 要 为探索二元碱度、MgO 和 Al O 对鲅鱼圈高炉炉渣性能的影响，进行了配渣实验研究及炉渣成分预测模 2 3 型开发工作，结果表明，在鲅鱼圈高比例进口矿条件下，其合理造渣制度为碱度小于 1.17，(MgO)含量在 9%左右， (Al O )含量小于 16%，（Al O ）/ （SiO ）0.45 。开发的炉渣成分预测模型可预算炉料结构发生改变，尤其是进口 2 3 2 3 2 块矿比例和 Al O 含量波动大的矿种变化时炉渣成分。 2 3 关键词 炉渣黏度 熔化性温度 造渣制度1 Study on Proper Slagging Regime of Ansteel Bayuquan Subsidiary Blast Furnace Guo Tianyong Che Yuman Li Chunming Sun Peng Li Xiaowei Li Liancheng Yao Shuo (Ansteel Limited Company , Anshan, 114009) Abstract An experimental study on BF slag has been carried out in lab scale, and the effect of dual basicity and MgO on slag has been studied. The composition of reasonable slag for a high proportion purchasing iron ore was that basicity and Al O were less than 1.17 and 16% separately, MgO about 9%, and (Al O ) /(SiO ) no more than 0.45. A mathematical 2 3 2 3 2 model to predict BF burden structure was developed. Key words viscosity of slag, melting temperature,slagging regime 鞍钢鲅鱼圈分公司高炉原料以进口矿为主。随着国际铁矿石资源供应紧张，进口铁矿石产地和品种不断 增加，造成铁矿石品质下降，成分相差悬殊，特别是一些进口矿 Al O 含量偏高，导致高炉渣 Al O 含量上 2 3 2 3 升，炉渣黏度升高，流动性变差，炉况顺行破坏，焦比升高。因此，如何将高炉渣 Al O 含量控制在合理范 2 3 围，从而克服高Al O 含量炉渣给高炉顺行带来的不利影响，进而扩大高 Al O 劣质矿使用比例，降低高炉 2 3 2 3 生产成本具有重要研究意义。本文以鲅鱼圈分公司高炉实际炉渣为基准，通过配渣研究二元碱度、MgO 和 Al O 含量对炉渣性能的影响，从而确定使用高比例进口矿合适造渣制度，根据物料