镀锌锌渣完全回收技术与研究.pdfVIP

镀锌锌渣的完全回收技术研究1 1，2 1 1 1 1 卜二军 李玉银 朱文玲 徐 晓 王晓晖 （1.河北钢铁集团有限公司邯郸分公司, 邯郸 056015 ；2.东北大学，沈阳 110004 ） 摘 要 通过分别研究铝法再生回收工艺和蒸发冷凝法生产高纯度、高活性的锌粉工艺，实现资源的综合利用，并 得以在工业上应用。探索从锌渣中连续制备锌粉的工艺方法，解决锌渣传统回收工艺中存在的问题和不足。 关键词 热镀锌渣 综合利用 锌粉 冷凝法 Study on Zinc Regeneration Technology from Zinc Slag During Hot-dip Galvanizing Process Bu Erjun1,2 Li Yuyin1 Zhu Wenling1 Xu Xiao1 Wang Xiaohui1 (1. Hebei Iron and Steel Group，Handan Iron and Steel Company, Handan, 056015; 2.Northeastern University，Shenyang, 110004) Abstract The research on zinc regeneration technology by “Aluminum Processn” and evaporated-condensation method to produce high purity, high activity zinc powder, to realize the comprehensive utilization of resources in industry. Explore the technology to extract Zinc powder continuously from zinc slag, solve the zinc slag traditional recovery process of existing problems and deficiencies. Key words hot-dip galvanizing slag, comprehensive utilization, zinc powder, condensation method 1 引言 邯钢锌渣是镀锌生产线热镀锌锅产生的浮渣，主要来源是酸洗镀锌厂和冷轧厂，年产锌渣量约为 3000t，含 锌量为 90%~95%，是极高的金属锌再生资源。目前我公司对锌渣处理方式主要为直接低价销售，经济效益低。 利用锌渣制备附加值较高的产品已经成为人们研究的重点，若将镀锌锌渣完全回收利用将带来巨大利润。因此, 合理而有效地回收、利用锌渣废料是一件“变废为宝,化害为利”的益事，对社会的可持续发展具有重大意义。 目前锌渣回收的方法主要有电解法、蒸发凝聚法、化学法等。利用电解法进行分离提纯，主要通过阴极析 出的锌熔融后加工成锌锭，缺点是在生产过程中需要使用酸溶剂，耗电量较大，耗酸量也较大，对设备腐蚀较 严重[1]。真空蒸馏回收锌渣缺点是真空维护难度大，设备的使用寿命较低，并且是间断加热和间断作业，产量低， 难以形成大规模工业化生产[2]。在权衡不同方法的优缺点后，最终我们采用铝法再生回收工艺和蒸发冷凝工艺。 2 原料分析 2.1 化学成分 试验用的镀锌锌渣是在热镀锌生产过程中在锌锅表面产生的浮渣，一般含锌量在 90% 以上，主要杂质 卜二军（1979—），男，2009 年在东北大学攻读博士，在邯郸钢铁集团技术中心工作，工程师，主要从事资源综合利用工作，buerjun@ 镀锌锌渣的完全回收技术研究 是铁和铝，其化学成分见表 1： 表 1 锌渣的化学成分（% ） 厂名 Zn Al Fe Si Ca