Ag-Cu-Si合金的熔化特性.pdf

贵金属990404 贵金属 PRECIOUS METALS 1999年 第20卷 第4期 Vol.20 No.4 1999 Ag-Cu-Si合金的熔化特性 罗锡明 摘　要　用DTA法测定Ag-Cu-Si合金中(CuAgx) )- 100-y 5 Ag 7个特定成份伪二元系的固相线、液相线。结果表明，Si含量对Ag-Cu合金液相线温 度及熔化间隔Δt的影响是显著的。在研究的Si名誉含量0～10wt%，其液相线 呈“V”型变化。Δt值小对于钎料合金选择和降低Ag含量是有利的。 关键词　银基合金，液相线，固相线 分类号　TG146.32 Melting Characterization of Ag-Cu-Si Alloys Luo Ximing (Kunming Institute of Precious Metals，Kunming 650221, China) Abstract　The Liquidus and solidus of pseudobinary of seven special compositions,(CuAgx) -Siy(x=10,20,30,40,50,72)and (CuSi )-Ag,in the ternary Ag-Cu-Si alloy system were 100-y 5 determined by DTA.The results indicated:the influence of Si content on the temperature of Liquidus of Ag-Cu alloy and melting interval( Δt)was apparent,the liquidus appeared “V ”- type variation within the range of Si contents 0～10wt%,and smaller ΔT values were of benefit to select filler metal of alloy and to reduce Ag content. Keywords　Ag-Cu-Si alloy,Liquidus,Solidus 1　引　言 ［1，2］ 　　Ag-Cu及Ag-Si二元系均是简单共晶系，其相关研究已多次报道。Ag-Cu 及 ［3］ Ag-Si 二元系的共晶组成和共晶温度分别为x(Ag)=60.2%，779.1℃和x(Ag)=89%， 835℃。Cu-Si二元系是较为复杂的体系，存在两个共晶转变点，相结构亦较为复杂， ［4］ 共由6个相组成，体系的复杂区集中在富Cu端 。Ag-Cu-Si三元系相图还未见报道。 -6 ［5～8］ Pa)、在不锈钢母材上漫流性优良的Ag-Cu-Si三元系合金钎料 ， 气压≤1.33×10 但上述文献未有Ag-Cu-Si系的熔化特性报道。 　　为了在电真空钎料中开发和利用Ag-Cu-Si系合金，本文阐述了Ag-Cu-Si合金系中7 个特定成份合金伪二元系的固相线和液相线温度，为在Ag-Cu-Si系中开发中温电真空 钎料提供依据。 万方数据 file:///E|/qk/gjs/gjs99/gjs9904/990404.htm（第 1／8 页）