END疲劳小裂纹的萌生和扩展形态研究.pdf

·76 · 现代机械 　2009年第 6期 　　 ( ) 文章编号: 1002 - 6886 2009 06 - 0076 - 03 疲劳小裂纹的萌生和扩展形态研究 1 2 何子淑 ,粱益龙 ( 1. 贵州工业职业学院, 贵州 贵阳 550008; 　2. 贵州大学 ,贵州 贵阳 550003) 摘要:本文通过对 35SMi nMoV 复相钢的常温疲劳试验研究和 GH4049镍基高温合金的高温疲劳试验研究,获得了大量的试验数 据和得出了相应的裂纹扩展行为规律 。采用对比分析方法 ,从疲劳小裂纹的萌生和扩展形态出发 ,归纳总结了疲劳小裂纹的扩 展规律。 关键词 :对比分析　疲劳小裂纹　萌生　扩展形态　扩展规律 中图分类号: TG115. 57, TG146. 15　　文献标识码 :A Study on the Beg inn ing and D evelopm en t Behav ior of Sma ll Fa tigue Cracks HE Z ishu, L IANG Y ilong Abstract: The thesis studied the fatigue test of 35SMi nMoV steel at normal temp erature and the N ibase sup er alloy GH4049 at high tem p erature. During the studies, a number of trial data and exp anding regu lation of fatigue crack s were obtained. In contrast w ith the beginning and develop ment behavior of small fatigue crack s, we conclude a series of exp anding regulation of small fatigue crack s. Key words: contrast analysis ; small fatigue crack s; beginning; development behavior; exp anding regu lation 0　引言 工程中对疲劳长裂纹的研究有多年的历史 ,得到的结论 和提出的疲劳裂纹扩展规律有很多,但是对疲劳小裂纹的试 验研究仍然没有较为系统的结论 ,因此本文采用对比分析的 方法 ,将高温小裂纹的试验结果与常温小裂纹研究结论进行 适当的对比,找出疲劳小裂纹的萌生位置和扩展形态及影响 因素 ,分析总结出有关疲劳小裂纹萌生和扩展规律。 1　疲劳小裂纹的萌生研究 11疲劳小裂纹的萌生位置观察 由图 1的断裂扫描 12疲劳小裂纹的萌生规律研究 图片看出,疲劳小裂纹 试验结果表明,疲劳小裂纹一般萌生于应力集中的地 在缺口部分的应力集中 方 ,如半圆形缺口底部的晶界处或缺口底部的夹杂物和孔洞 小孔的边缘沿着晶界萌 处 ,高温下的这种特性尤其明显。所以高温下的疲劳小裂纹 生。由复型照片图 2、图 ( ) 多数萌生于半圆形缺口底部的晶界