Mod.9Cr1Mo钢微合金化规律的热力学解析.pdfVIP

_______________________________________________________________________________ Mod.9Cr-1Mo 钢微合金化规律的热力学解析 1 2 2 2 2 宛农 ，谢锡善 ，张家福 ，徐志超 ，董建新 （1. 武汉工业学院，武汉，430023 ；2. 北京科技大学，北京，100083） 摘要：本文从热力学角度出发，以图解的方式直观地揭示了 Mod.9Cr-1Mo 钢中碳、氮、铝、 钒和铌等微量元素之间的交互作用及其对强化相析出的影响规律。分析结果表明在高温服役 过程中，钢中较低的铌、钒和铝含量与较高的 N 含量配合有助于增加 VN 相的弥散析出和 抑制 M23C6 相的粗化速度，其结论与实际相符。 关键词：Mod.9Cr-1Mo 钢，微合金化，热力学，解析 Thermodynamic Resolution of Microalloying Law of Mod.9Cr-1Mo Steel 1 2 2 2 2 WAN Nong , Xie Xishan , Zhang Jiafu ，Xu Zhichao , Dong Jianxin (1.Wuhan Polytechnic University, Wuhan 430023, China ； 2. University of Science and Technology Beijing, Beijing 100083, China ） Abstract:. Interaction of minor elements in Mod.9Cr-1Mo steel, such as C, N, Al, V and Nb, and their effects on the precipitating behavior of strengthening phases were revealed by graphics based on thermodynamics theory. The results shows that lower contents of Nb , V as well as Al and upper content of N in Mod.9Cr-1Mo steel is favorable to the dispersal precipitation of VN phase and the suppression of M23C6 carbide coursening process during high temperature service, which are consonant with actuality. Key words: Steel Mod.9Cr-1Mo; Microalloying; Thermodynamics; Resolution 现代合金钢通常加入了多种微合金元 温度为 T 时的溶度积KS 可以用下式表示： 素以满足某项或多项特定性能的要求，为获 LnK i j S=Log[M] [X] =A/T+B (1) 得良好的高温持久性能，在 9Cr-1Mo 钢基础 式中，[M]—在绝对温度为 T 时合金元素M 上加入钒、铌和氮进行微合金化而发展起来 的溶解度，wt.% ； 的 Mod.9Cr-1Mo 钢便是其中一个典型的例 [