中间合金铸造组织遗传性研究.docVIP

中间合金铸造组织遗传性研究 摘要：冶金组织遗传性是指金属及其合金的组织受原材料金属组织的影响，铝及铝合金显微组织的偶发性缺陷往往与冶金组织遗传性有关，铝及铝合金的冶金组织遗传性，以及它对材料的组织与性能的影响。本文概述了铸造过程中原料组织遗传现象的概念及其发展过程，讨论了组织遗传过程中的遗传因子以及对遗传效应的评价，分析了原料组织遗传性对铸造铝合金组织性能的影响。指出通过选用优质原材料，优化熔体处理工艺，研究开发新工艺等，可以控制或利用原料的组织遗传效应，从而提高铸造铝合金的性能Genetic refers to the organization of the metals and their alloys metallurgical group is affected by raw material metal organization, aluminium and aluminium alloy microstructure of accidental defect often related to metallurgical group inherited, genetic, metallurgy of aluminium and aluminium alloy organization and its effect on microstructure and properties of materials. In this paper, the raw material in the process of casting organization concept and development process of genetic phenomenon, discussed the genetic genetic factor in the process of organization, and evaluation of genetic effect, analyzed the raw material organization genetic influence on casting aluminum alloy organization performance. Pointed out that by choosing high quality raw materials, optimization of melt treatment process, the research and development of new technology, etc., can control or use of the organization genetic effect of raw material, so as to improve the performance of casting aluminum alloy Keywords:Casting of aluminium alloy genetic organization and performance  第一章 绪论 3 1.1 中间合金铸造遗传性的概论 3 1.2 中间合金铸造遗传性的现状及发展 3 1.3遗传性概述 4 第一章 实验方法 4 2.1 原材料 4 2.2仪器设备 5 2.3实验方案 5 第二章 结果分析 6 3.1 组织分析 6 3.1.1原始组织分析 6 图1 原始50×10倍 6 图2 原始20×10倍 6 3.1.2细的Al-10Fe晶粒 6 图3 原始80×10倍 7 图4原始50×10倍 7 3.1.3 Al-10Fe炉冷组织及冷却速度分析 7 图5 Al-10Fe炉冷组织20×10倍 8 图6 Al-10Fe炉冷组织50×10倍 8 Figure 2 炉冷冷却速度分析 9 3.1.4 炉冷（粗的）AL-10Fe配成Al-1Fe铁模冷却（快冷）组织 9 图7 Al-1Fe铁模冷却组织 倍率10×50 9 图表 8 Al-1Fe铁模冷却组织 倍率10×50 10 3.1.5 铁冷（细的）AL-10Fe配成Al-1Fe铁模冷却（快冷）组织 10 图9铁冷AL-10Fe配成Al-1Fe铁模冷却组织 倍率10×50 10 图10铁冷AL-10Fe配成Al-1Fe铁模冷却组织 倍率10×20 10 3.1.6 炉冷（粗的）AL-10Fe配成Al-1Fe空气冷却（慢冷）组织 11 图11