年产400万吨早强型高铝水泥工艺设计.doc

年产400万吨早强型高铝水泥工艺设计 Process Design of Early Strength High Alumina Cement with 400 million Tons Annual Output 学生学号 学生姓名 专业班级 指导教师 联合指导教师 完成日期 吉林化工学院 Jilin Institute of Chemical Technology摘 要 本设计任务是设计年产400万吨早强型高铝水泥生产线。主要是以铝矾土和石灰石为主要原料，加入适当比例的粉煤灰和石膏，采用熔融法生产高铝水泥。高铝水泥具有早期强度高、耐高温、抗渗性好等特点，在工业生产中有着广泛应用。本设计在熟练掌握了高铝水泥的生产原理、方法、工艺流程及国内外发展现状的基础上，经过物料平衡计算、热量衡算、窑的选型、物料的储存和均化、各生产设备工艺设计和主机选型、厂址选择及简单的技术经济分析等步骤。绘制图，编写了设计说明书和设计计算书。Abstract This design task is to design an annual output of 4 million tons of early strength of high alumina cement production line. Mainly based on bauxite and limestone as the main raw material, by adding an appropriate proportion of fly ash and gypsum, and use the melt produce of high alumina cement. Alumina cement with high early strength, high temperature resistance, impermeability, it has been widely used in industrial production. On the basis of mastered the principle of the production of high alumina cement, process and development in the world ,counted after the calculations of material balance, heat balance, the selection of the kiln, materials storage and homogenization, the production equipment process design and host selection, site selection, and simple technical and economic analysis . Draw a total of four diagrams,they are kiln inlet section, kiln inlet basic plan, the total plant layout plan, kiln process flow and the preparation of design specifications and design calculations. Key Words：Alumina cement; NSP cement;Rotary kiln; Cement grinding摘 要 I Abstract II 第一篇 设计说明书 1 第1章 绪论 1 1.1设计任务及依据，产品概述 1 1.1.1 设计任务 1 1.1.2 依据 1 1.1.3 产品概论 1 1.1.3.1产品定义及用途 1 1.1.3.2产品的意义和价值 2 1.2厂址的选择 3 1.2.1厂址选择的依据 3 1.3建厂的原始资料 4 1.3.1原料资源 4 1.3.2地理位置 5 1.3.3气候特点 5 1.3.4水文状况 5 1.3.5矿区概况 5 1.3.6交通概况 6 1.3.7矿山矿石质量 6 1.4 岗位人员配置 6 第2章 生产工艺概述 8 2.1 工艺原理 8 2.2 生产方法 8 2.3工艺流程叙述 8 2.3.1石灰石破碎及预均化 8 2.3.2原煤的预均化 9 2.3.3 原料配料 9 2.3.4 原料粉磨 9 2.3.5 生料的均化 9 2.3.6 熟料烧成 10 2.3.7 熟料储存 10 2.3.8 煤粉制备 10 2.3.9 石膏、混合材储存及输送 10 2.3.10 水