Aluminum.doc

Alclad Aluminum 7075-T6, T651 Subcategory: 7000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal Close Analogs: Composition Notes: Composition for AA 7075 (not Alclad 7075 specifically).Aluminum content reported is calculated as remainder.Composition information provided by the Aluminum Association and is not for design. Key Words: Alclad 7075-T6, T651; Alclad 7075-T6, T651 Component ???Wt. % Al 87.1 - 91.4 ? Cr 0.18 - 0.28 ? Cu 1.2 - 2 ? Fe Max 0.5 ? Component ???Wt. % Mg 2.1 - 2.9 ? Mn Max 0.3 ? Other, each Max 0.05 ? Other, total Max 0.15 ? Component ???Wt. % Si Max 0.4 ? Ti Max 0.2 ? Zn 5.1 - 6.1 ? Material Notes: Data points with the AA note have been provided by the Aluminum Association, Inc. and are NOT FOR DESIGN. Click here to view available vendors for this material. Physical Properties Metric English Comments Density 2.81?g/cc 0.102?lb/in? ?For AA7075 (Not Alclad) Mechanical Properties Ultimate Tensile Strength 524?MPa 76000?psi ?AA; Typical Tensile Yield Strength 462?MPa 67000?psi ?AA; Typical Elongation at Break 11?% 11?% ?AA; Typical; 1/16 in. (1.6 mm) Thickness Modulus of Elasticity 71.7?GPa 10400?ksi ?AA; Typical; Average of tension and compression. Compression modulus is about 2% greater than tensile modulus. Shear Strength 317?MPa 46000?psi ?AA; Typical Processing Properties Annealing Temperature 413?°C 775?°F ? Solution Temperature 466 - 482?°C 870 - 900?°F ? Aging Temperature 121?°C 250?°F Aluminum 7075-T6; 7075-T651 Subcategory: 7000 Series Aluminum Alloy; Aluminum Alloy; Metal; Nonferrous Metal Close Analogs: Composition Notes: A Zr + Ti limit of 0.25 percent maximum may be used with this alloy designation for extruded and forged products only, but only when the supplier or producer and the purchaser have mutually so agreed. Agreement may be indicated, for example, by reference to a standard, by letter, by order note, or other means which allow the Zr + Ti limit.Aluminum content reported is calcu