双向拉伸BOPP薄膜生产 毕业论文.doc

摘要 分析了BOPP薄膜生产过程中的取向和结晶对薄膜机械力学性能和光学性能的影响，实际生产中生产工艺应该根据PP的热力学特性相应调整，以制造出双向取向度高，同时结晶微细、均匀的高性能优质BOPP薄膜。 关键词 取向，结晶，BOPP薄膜 Abstract The Orientation and Crystallization in Producing BOPP Film Wu Zengqing, Tu zhigang (Zhanjiang Packaging Material Enterprises Ltd., Guangdong, 524022) ABSTRACT：The influences of the orientation and crystallization in producing Bi-axially Oriented Polypropylene (BOPP) film on mechanic properties and optic properties are analyzed. In order to produce high-quality BOPP film with high bi-axially orientation degree and superfine uniform crystal the processes of BOPP film should be adjusted based on the thermodynamic properties of PP in the course of practical production. KEYWORDS: Orientation, Crystallization, BOPP film 目? 录绪? 论………………………………………………………………..…………2 第二章 原材料性能………………………………………………………..……………..…3 第三章BOPP薄膜的主要生产方法及工艺流程……………………………………………..3 第四章 取向……………………………………………………………………………………4 4．1 流动取向 4．2拉伸取向 第五章 温度对BOPP薄膜生产的影响…………………………………………………..……6 5．1 冷辊温度的控制 5．2 纵向拉伸温度 5．3 横向拉伸温度 第六章 结晶……………………………………………………………………………………7 6．1结晶对生产工艺调整的影响 6．2结晶对BOPP性能的影响 第七章 BOPP薄膜生产中常见的问题及解决办法…………………………………..………8 7．1铸片常见的缺陷和解决办法 7．2拉伸破膜的原因及解决办法 第章 结论与展望…………………………………………………………………………10 8．1 结论 2 展望 …………………………………………………………………………11 绪? 论 对于一种包装材料而言，反映外观美感的光学性能和反映使用承受强度的机械力学性能是非常重要的性能指标。聚丙烯（PP）是一种结晶性聚合物，在BOPP薄膜的加工过程中，PP在力、热和电场等的作用下，经历了复杂的取向和结晶的变化，PP聚集态结构中的取向和结晶将对BOPP薄膜光学性能、力学性能起决定性影响，因此如何通过工艺的调整，控制BOPP薄膜生产过程中的取向和结晶是改善产品品质、提高产品等级的关键。 第二章 原材料性能 工业化生产BOPP薄膜用主料的主要成分是PP。PP是一种典型的立体规整性聚合物，根据烃基在分子平面两侧的分布，可分为等规PP、间规PP和无规PP。等规PP和间规PP具有不同的结晶结构，等规PP是以均相成核的三维生长方式进行结晶，而间规PP主要以均相成核的二维方式进行结晶，形成了外观尺寸不规则的小晶片，而且由于间规PP分子结构的规整度较低，使得间规PP具有较低的结晶速率和结晶度。研究表明，等规度越大，结晶速率越快，薄膜产品的屈服强度和表面硬度会明显增大，而无规PP在聚合物中起内部润滑剂的作用，并有利于聚合物定向，有助于改善薄膜的光学性能。 目前，BOPP薄膜品种繁多，性能也差异很大，造成这种情况的主要原因是使用的原料和生产工艺不同。实践证明，只有等规PP的质量分数为95%～97%，无规PP的质量分数为3%～5%的PP才适合生产BOPP薄膜，并且一般选用熔体流动速率为2～4g/10min的PP。另外，通过在PP薄膜的表面上共挤出一层或多层熔点较低的共聚物，可以扩大BOPP薄膜在包装工业中的应用范围。 第三章BOPP薄膜的主要生产方法及工艺流程 目前BOPP薄膜的生产方法主要有管膜法和平膜法。管膜法属双向一步拉伸法；平膜法又分为双向一步拉伸