高分子材料加工技术专业 毕 业 论 文 材料工程系 PVC热稳定性研究 〖关键词〗: PVC 热稳定性 热稳定性研究 影响因素 〖摘要〗: 讨论了影响PVC热稳定性的因素，提出了提高加工热稳定性的研究重点。对影响PVC热稳定性的各种因素诸如原料、氧、电导率、分散剂和搅拌等，采用链转移剂、降低聚合度、保持适当的PVC反应温度等是抑制羰基烯丙基生成的重要措施。同时加入适当的热稳定剂也是提高PVC热稳定性的重要手段，在新时期PVC热稳定性的增强可以明显改善其使用性能，对生产生活的影响意义重大。它也是今后PVC研究中很重要的一部分。 Research of PVC thermal stability Li Zhi hua Keywords: PVC thermal stability thermal stability study factors Abstract：Discusses the influencing factors of PVC thermal stability, and puts forward the improvement of the machining of thermal stability are discussed. The influence of various factors of PVC thermal stability, such as raw materials, oxygen, conductivity, dispersants and agitation, using chain transfer agent, reduce the degree of polymerization, maintain proper PVC reaction temperature, etc is inhibiting carbonyl allylic generated important measures. Add the proper heat stabilizers is also raises an important means of PVC thermal stability in the new era, the stability of PVC thermal can obviously improve the use of enhanced performance; to the influence of production and life of great significance. It but also the future of PVC very important part in research. 目 录 前言 PVC是世界五大通用塑料之一，广泛应用于建筑，轻工业品，电线电缆，医药和农业等国民经济许多领域。聚合物分子链上的结构缺陷是导致树脂热稳定性差的主要原因。提高热稳定性性能，是改善制品质量和拓宽其应用范围的有效保证。因此研究如何提高热稳定性性能有其重要的意义。 PVC树脂的热稳定性在加工过程不但影响制品外观、而且还会影响加工设备以及制品的其它性能。由于其聚合机理决定了该类树脂在结构上存在先天缺陷，普遍通过在生产后期或加工过程中添加热稳定剂来提高其热稳定性。但从树脂合成源头采取措施，采取尽可能改善树脂热稳定性的合成工艺及注意事项，对提高树脂品质依然具有重要价值。 聚氯乙烯的自由基聚合原理决定了其分子链中无序结构的存在，而 C-Cl 键的低键能结构特征决定了其是热不稳定的聚合物。PVC 在加工过程中表现出来的热稳定性能及加工性能远低于与其主链结构相似的 PE。PVC 在 100℃就开始分解放出氯化氢，170℃左右即明显分解，而聚氯乙烯制品的加工通常都是在170℃以上进行，为了保证聚氯乙烯在后加工过程中能顺利成型、并且生产出的制品满足使用需要，这就要求聚氯乙烯树脂有较高的热稳定性能，在后加工过程中能经受加工温度的考验，保证制品的物理机械性能满足使用的要求树脂结构， 特别是不稳定的异常结构对其性能，特别是热性能的影响较大。 异常结构包括： 1、头-头结构：它可以通过两种途径形成：两个自由基链的偶合终止反应以及链增长反应中的异常头头加成反应。2、未端双键：在大分子自由基双基终止过程中的歧化终止可以产生链端不饱和键。3内部双键：其产生是在聚合过程中由于链自由基向大分子转移并进一步脱氯而形成的。4、共轭双键（多烯结构）：它们多形成于 PVC 的热降解过程。 5、烯丙基氯结构：据文献介绍该结构与叔 氯组成的