阴极电泳涂料的制备研究 摘要 阴极电泳涂料作为一种环保型的水性涂料,具有广阔的应用前景。在此采用封闭的甲苯二异氰酸酯作为固化剂制得了环氧树脂阴极电泳涂料,同时对环氧树脂阴极电泳涂料的配方和工艺、电泳涂装过程进行了研究，探讨了合成树脂的反应条件,并对所得阴极电泳涂料的性能进行了测试。结果表明,在适宜的电泳工艺参数下,可以得到外观光滑平整,综合性能优良的漆膜,并系统地探讨了电泳工艺参数对涂膜性能的影响。 关键字：阴极电泳涂料，环氧树脂，封闭交联剂，漆膜 Abstract As an environment-protecting water-borne coating , the catholic electrophoretic coating has wide application prospects. The cathodic electrophoretic coating of epoxy resin was prepared with blocked isocyanate as curing agent . and the formulation, technology, electrophoretic coating process of the title coatings was discussed，reaction condition of the synthesis of resin was investigated ,and properties of the obtained electrophoretic coating were tested. The results show that the coating film with flat , smooth and excellent performance can be obtained under the condition of appropriate electrophoretic parameters. The influence of the parameters of electrophoretic process on the properties of paint films were studied systemically. Key words： cathodic electrophoretic coating；epoxy resin；locked crosslinking anent；paint film 1 文献综述 1.1 阴极涂料发展概述 1.1.1涂料的应用和发展 涂料的应用始于史前时代，我国使用生漆和桐油作为涂料至少有四千年历史。虽然涂料的应用与生产有着漫长的历史，但它只是以一种技艺的形式相传。现在的涂料自然已不是旧时的模样，它己经进入了科学的时代。涂料第一次和科学的结合是二十世纪二十年代杜邦公司开始使用硝基纤维素作为喷漆，它的出现为汽车提供了快干、耐久和光泽度好的涂料。 三十年代W:HCarothes以及其后他的助手P..JF10yr对高分子化学和物理的研究，为高分子科学的发展奠定了基础，也为现代涂料的发展奠定了基础，此后涂料工业便和高分子科学的发展结下了不解之缘[l]。 三十年代开始有了醇酸树脂，后来它发展成为涂料中最重要的品种一醇酸漆。第二次世界大战时期，由于大力发展合成乳胶，从而为乳胶漆的大规模应用开辟了道路。四十年代Ciba化学公司等发明了环氧树脂涂料，它的出现使防腐涂料有了突破性进展。五十年代开始使用丙烯酸涂料，由于丙烯酸涂料具有优良的性质，如优越的耐久性和高光泽，结合当时出现的静电喷涂技术，使汽车漆的发展又上了一个台阶，例如出现了高质量的金属闪光漆。五十年代FordMotor公司和Gldiden油漆公司发展了阳极电泳漆，以后PPG又发展了阴极电泳漆。电泳漆不仅是一种低污染的水性漆，而且进一步提高了涂料防腐蚀的效果，为工业涂料的发展作出了贡献。六十年代又出现了聚氨酯涂料，它可以室温固化，而且性能优异，是最有前途的现代涂料品种之一。其后粉末涂料以及纳米材料在涂料中的应用也逐步得到了发展。 1963年美国福特公司在PPG公司的帮助下建立了世界上第一条完整的电泳涂漆生产线。这被称为电泳涂装史上的第一里程碑。随着新型电泳涂料的开发和涂装工艺的进步，尤其是20世纪70年代初期阳极电泳涂料和阴极电泳涂装技术的开发，电泳涂料在汽车工业上得到迅速普及，目前，90%以上的汽车涂漆采用的是阴极电泳涂料［2］。 目前，涂料研究的方向其一是涂料应用的自动化，所提供的产品施工简便和安全，特别是产品涂装的自动化；其二是向环保型涂料方向发展；其三是增加新的组成成分，使涂料在涂