UV光固化含磷丙烯酸酯单体的合成详解.doc

UV 光固化含磷丙烯酸酯单体的合成 Synthesis of UV curable acrylate monomers containing phosphorus UV 固化含磷丙烯酸酯单体是具有阻燃性质及光固化活性的含磷丙烯酸类单体。它是由环状磷酸酐（2-甲基-2，5-二氧-1，2-氧磷杂环戊烷，OP）与含有羟基的丙烯酸酯单体进行酯化反应生成的。本论文探讨了合成过程中温度、催化剂、投料比和反应时间对转化率的影响，实验证明：最佳反应温度为110℃，最佳催化剂为PK208LH，用量为20g/mol，OP与丙烯酸羟丙酯的物质的量比为1:1，最佳反应时间为5h。在这种反应条件下，反应产物产率是最高的，可达到98.12%。而且将含磷丙烯酸酯与聚氨酯丙烯酸酯6170进行复配后，通过垂直燃烧实验测量其阻燃性能后发现：当含磷丙烯酸酯含量大于63.33%后，其阻燃级别为V-0级。 hosphorus-containing acrylate monomer has flame retardancy and UV curing activity, which is prepared by the esterification of the cyclic anhydride phosphate (2-methy-2,5-dioxo-1,2-oxaphospholane, OP) with hydroxypropyl acrylate monomer. The effects of temperature, catalyst, feed ratio and reaction time on the yield of product are investigated. The results show that the optimal reaction temperature is 110℃, optimal catalyst is PK208LH and its optimal content is 20g/mol, the best molar ratio of OP and hydroxypropyl acrylate is 1:1.2, and the optimal time is 5h. Under this condition, the yield of the reaction product is the highest, can reach 98.12%. Then, the phosphorus-containing acrylate monomer and polyurethane acrylate 6170 are used to prepare UV curing resin. The UL94 test V-0 rating is achieved by addition of 63.33 wt.% the phosphorus-containing acrylate monomer. Keywords Cyclic phosphoric anhydride；UV light curing；Optimization of conditions；Flame retardant 1绪论 1 1.1研究背景及意义 1.2反应单体及产物的简介 1.2.1 环状磷酸酐简 1.2.2 含羟基的丙烯酸酯简介 1.2.3 UV固化含磷丙烯酸酯单体简介 1.3 3D打印技术简介 1.3.1 3D打印技术的概念 1.3.2 SLA技术的简介UV光固化材料分类UV光固化材料优点 1.3.3 应用与发展趋势 1.4 含磷丙烯酸酯单体的阻燃 1.5研究目的及方法 1.5.1研究目的 1.5.2研究方法 2 实验部分 2.1 实验原料及仪器 2.1.1实验原料与试剂 2.1.2主要仪器及设备 2.2 含磷丙烯酸酯的合成 2.2.1 反应原理 2.2.2 OP的提纯 2.2.3 合成方法. 1 2.2.4产物的萃取 3 实验结果与讨论 3.1反应条件的优化 3.1.1反应温度的影响 3.1.2反应时间的影响 3.1.3催化剂种类的影响 3.2含磷丙烯酸酯单体的结构表征3.3光敏树脂的测试 3.3.1光敏树脂配方组成 3.3.2拉伸强度的测试 3.3.3固化时间的测试 3.3.4凝胶率的测试 3.3.5粘度的测试3.3.6 阻燃性能的测试 4结论 致谢 参考文1绪论 1.1 研究背景及意义 美国学者杰里