混凝土腐蚀与防护.doc

混凝土腐蚀与防护 摘要 混凝土的碳化作用，O2 、H2O及其它侵蚀性介质的渗入，所选材料，所处环境等各种因素都会影响混凝土结构的耐久性，延长混凝土使用寿命的关键是降低空隙率、提高渗透能力。本文从腐蚀类型、材料选择和配比、施工要求、表面改性等方面，对混凝土的防护方法进行了详细的分析、论述。在已有混凝土结构的表面涂覆一层稳定、抗渗的涂层，是被广泛采取的保护措施。针对不同应用环境，综述了选择涂层的种类和厚度，并介绍了混凝土涂料的发展方向。 关键词 混凝土结构 腐蚀 防护方法 涂料 Concrete Corrosion and Protection Du Moyuan Abstract Concrete carbonation, O2, H2O, and other aggressive media penetration, selected materials, their environment, and other factors will affect the durability of concrete structures to extend the service life of concrete key is to reduce porosity and improve the penetration capability. In this paper, types of corrosion, material selection and proportioning, construction requirements, surface modification, etc., of concrete protection methods carried out a detailed analysis of discourse. The surface of the existing concrete structure coated with stable, impervious coatings are widely adopted protective measures. For different applications, review the selection of the type and thickness of the coating, and introduces the development direction of concrete coatings. Keywords： concrete structure coating corrosion protection methods 1.前言 混凝土的定义： 广义：是指由胶凝材料、粗细材料、水等材料按适当的比例配合，拌合制成的混合物，经一定时间后硬化而成的坚硬固体。最常见的混凝土是以水泥为主要胶凝材料的普通混凝土，即以水泥、砂、石子和水为基本组成材料。 狭义：素混凝土（不添加钢筋），由水泥、砂、水和石子组成。 钢筋混凝土是以波特兰水泥的水化物【主要是水化硅酸钙（3CaO.2SiO2.3H2O）】O3.6H2O+3(CaSO4.2H2O)+20H2O=(3Cao),Al2O3.3CaSO4.32H2O （4）镁盐的影响 镁盐在渗入混凝土中后将与Ca(OH)2发生反应，使混凝土中的碱度降低，水泥中的水化硅酸钙和水化铝酸钙便易与呈酸性的镁盐反应，所生成的Mg(OH)2还能与铝胶、硅胶缓慢反应，结果使水泥石粘结力减弱，混凝土强度降低。 （5）环境的温度、湿度和冻融交替频度严重的影响着混凝土耐久性。当温度高于40摄氏度、湿度大于90%时，将使混凝土加速破坏。冻融交替得越频繁、混凝土受到的危害就越大。 3生物作用的影响 类似于混凝土的化学腐蚀，如流化细菌利用下列反应： 2S+SO2+2H2O=2H2SO4 将S转变成H2SO4，从而引起混凝土的硫酸盐腐蚀。 4.混凝土结构的防护方法 提高混凝土构筑物的抗蚀性和耐久性，一方面要遴选优质材料，确定适当配比，提高施工水平，以改善混凝土结构本身的密实性；另一方面，要将混凝土构筑物与周围腐蚀介质隔离开来，以保护混凝土不受其侵蚀。为此目的，宜采取如下措施。 A改善混凝土本身结构 使用普通混凝土时，应针对不同环境选用不同水泥，如在酸性环境中选用耐酸水泥，在海水中选用耐硫酸盐水泥和普通硅酸盐水泥等；增加混凝土中水泥用量，并且适当提高水泥中C3A的含量，但应低于8%；降低水灰比，控制灰砂比；掺入引气剂、膨胀剂、减水剂、防水剂、粉煤灰和矿渣等外加剂，可以显著改善混凝土的抗渗和耐久性；进行合理的搅拌、振实和充分的湿养护。 使用高性能混凝土。高性能混凝土是基于结