斜拉索防腐措施探讨.docVIP

斜拉索防腐措施探讨 　　摘要：斜拉索桥跨度较大，造型优美，是目前被广泛应用的桥型。斜拉索是斜拉桥的主要承重传力结构件，主要由高强度钢丝和锚固构成。由于其长期置于江河湖海不利外部条件下，导致钢丝和锚索结构件极易被腐蚀，严重影响桥梁的美观和使用寿命。如何采取方法防止斜拉索的腐蚀是桥梁工作者要研究的重要课题。本文首先分析了斜拉索腐蚀的原因，对斜拉索原材料的防腐要求进行了说明，重点探讨了斜拉索的防腐措施，最后从检测和新材料应用方面探讨了斜拉索防腐的保证措施。 　　关键词：斜拉索；防腐；腐蚀；锚具；新材料 　　Abstract: sew cable bridge span bigger, beautiful design, is the widely application of the bridge. Stayed cables, cable stayed bridge main bearing transmission structure, which mainly consists of high strength steel wire and anchorage composition. Because of its long-term in rivers, lakes and seas adverse external conditions, resulting in wire and cable structure can be corrosion, the serious influence of the bridge is beautiful and service life. How to take method to prevent the corrosion of stay-cables bridge is workers to study important issue. This paper first analyzes the sew line the reason of corrosion of the raw material of stay-cables anti-corrosion requirements are illustrated, and probes into the sew line of anti-corrosion measures, and finally from the detection and new materials application discusses stay-cables anti-corrosion measures to guarantee. 　　Keywords: sew line; Corrosion; Corrosion; Anchor; The new material 　　中图分类号： TG174.42 文献标识码：A 文章编号：2095-2104（2012） 　　一、斜拉索易被腐蚀的原因 　　斜拉索长期处于跨江河、跨海湾的地域，长期暴露在风雨、潮湿和污染空气的环境中，且主要材料为钢材，若防护不当，极易受到腐蚀。斜拉索的腐蚀主要是索体中的钢材与周围介质发生电化作用，造成氧化还原反应所致。引起斜拉索腐蚀的常见因素有空气、水、氯离子以及持续作用于高强钢丝的拉应力等，这些因素都会引起钢材腐蚀，产生应力腐蚀裂缝和氢化断裂。在斜拉索钢丝中的合金元素、渗碳体及其它杂质往往构成阴极，铁元素构成阳极，当斜拉索表面凝结吸附水汽而形成水膜时，就构成了无数微电池，空气中的氧、二氧化硫及二氧化碳等还会不断地溶解到水膜中去，促进铁元素电离，加快钢材的腐蚀速度，最终致使斜拉索被腐蚀。 　　二、斜拉索原材料的防腐要求 　　 （一）高强度钢丝的防腐蚀 　　高强钢丝是拉索的重要原材料。在电化学腐蚀中，处于阳极的金属首先被溶解，则会在钢丝表面镀上较活泼的金属。因此对斜拉索的钢丝采取热镀锌稳定化处理，要求镀锌层应均匀、连续、附着牢固，不允许有裂纹、斑痕和未镀上锌的地方。在斜拉索生产中，应对每批钢丝取不小于5%的盘数进行镀锌层质量检验，要求不得有裂纹、小刺、机械损伤、氧化铁皮、油迹和无连接点。镀锌层的单位重量不小于300g/m2。镀锌层的均匀性检验，应采用浸CuSO4溶液实验，要求不小于5次/min。镀锌层的附着力，要求在钢丝公称直径5倍的芯棒上缠绕2圈，以镀锌层不剥落为合格。 　　 （二）缠包带 　　对于热挤聚乙烯半平行钢丝拉索，为了便于其运输，用聚酯类薄膜复合缠包带将钢丝索缠包。缠包带除需要有足够的拉力强度和韧性外，还应对钢丝无腐蚀作用，其pH 值在61.5～81.5，防止加工好的缠包带受潮含水。 　　 （三）热挤PE护套 　　热挤PE护套是斜