某磷化废水处理工程实例.docVIP

某磷化废水处理工程实例 　　【摘要】：加工钢铁零件表面最常用的工艺是磷化处理，而其在废水中的量却比较高。本文介绍了青岛某磷化废水处理工程，该工程采用了RP反应器（反应与沉淀于一体设备）+砂滤器处理工艺。对RP反应器COD去除情况及重金属去除情况及磷酸盐去除情况及整体的运行效果进行了分析，当RP反应器的反应停留时间为15min，沉淀的停留时间为1h时，COD去除率可达80%以上，重金属的去除率可达90%以上，出水COD小于500mg/L，出水能够满足《污染物综合排放标准》（GB）中的三级标准。该处理技术取得了良好的经济与环境效益，可推广使用。 　　【关键词】：磷化废水；磷酸盐；化学沉淀 　　[ Abstract ] : the processing of iron and steel parts surface is the most commonly used is the process of phosphating treatment, and the waste water amount is relatively high. This paper introduces a Qingdao Phosphating Wastewater Treatment Project, the project uses RP reactor ( reaction and precipitation in one equipment ) + treatment of a sand filter process. The RP reactor COD removal and removal of heavy metals and phosphate removal and running effect of the overall analysis, when the RP reactor retention time was 15min, the residence time of precipitation was 1H, the removal rate of COD can reach more than 80%, heavy metal removal rate can reach above 90%, the effluent COD is less than 500mg\/L, the effluent to meet the pollutant comprehensive discharge standard ( GB ) in the three standards. The processing technology has made better economic and environmental benefits, and can be populari 　　[ keyword ]: Phosphating Wastewater; phosphate; chemical precipitation 　　中图分类号：X703文献标识码：A 　　磷化处理主要指的是在含有磷酸、磷酸二氢盐、其他化学助剂的酸性溶液中，使其金属表面转变为不溶性的、稳定的磷酸盐膜层的一种工艺[1]。它是金属抗蚀性能提高的有效方法。由于在进行磷化处理时，需要水洗、烘干，会产生大量的废水，而含量严重超标的是磷酸盐、COD及Zn2+等，如果将其直接排放，水体环境会受到严重污染，所以研究去除磷化废水中的酸盐、COD等污染物有重要的现实意义。 　　一 磷化废水中的成分 　　磷化处理在机械制造业中，通常的工艺流程的顺序是：除油、水洗、除锈、中和、调整表面、磷化、水洗、封闭表面、水洗、干燥[2]。产和珠磷化废水中，含量比较高的有磷酸盐、Zn2+、COD等，有较强的酸性。 　　产生污染物的原因是：①在进行磷化时，所使用的磷化液中有磷酸根、有机物、Zn2+等；②在加工零件时，所使用的抛光剂、防锈油，增加了石油类的含量；③在进行水洗时，所使用的清洗剂中含有表面活性剂，增加了有机物的含量；④磷化后的废水常混合于酸洗废水，使得磷化废水的pH值为2～4，为酸性。 　　二 处理磷化废水的方法 　　处理磷化废水的方法有很多，如化学方法、物理化学方法、生物方法等。物理化学法主要包括混凝沉淀、吸附法、反渗透等。生物法包括有活性污泥法等，其主要是通过微生物的生理活动，进行除磷的处理。但所有的方法在除磷时，均是把废水中的磷离子变为固体成份进行实现[3]。其固体成份主要有活性污泥中的微生物质、不易溶的金属盐沉淀等。这些固体与水体最终的分离还要经过沉淀、过滤、排泥等分离手段，这样才能从污水中将磷除去[4]。 　　三 磷化废水处理工程实例 　　1