土建工程概论论文 题目 浅谈新型建筑材料——煤矸石空心砖 学 生 姓 名 学 院 专 业 年 级 学 号 浅谈新型建筑材料——煤矸石空心砖 摘要： 煤矸石空心砖是一种新型环保墙体材料，是国家政策鼓励发展的新型建筑材料。利用煤矸石焙烧的空心砖具有较高的力学强度，又有较好的保温、隔热和防震性能，同时又可节约土地资源，减少环境污染，具有良好的市场前景。在生产过程中，必须按照工艺技术的要求进行操作，确保优质高产，同时要采取一定的措施，严格控制或避免对环境造成的污染。 关键词：煤矸石空心砖；新型；建筑材料；废料 Talking about a New-type Building Material——the Gangue Hollow Brick YANG Xiao-yu (China University of Mining and Technology, Environmental and Surveying College, Xuzhou 221008) Abstract: The gangue hollow brick, which is a new-type EP material, is a new building material encouraged to develop by the national policy. The gangue hollow brick, which has high mechanical strength, good insulation, heat insulation and shock performance can save the land resource and reduce the environmental pollution. This material has a good market prospect. The process of production must be in accordance with the requirements of technical operation to ensure high quality. Simultaneously some measures must be taken to strictly control or avoid the environmental pollution. Keywords: gangue hollow bricks; new-type; building materials; waste material 煤矸石是夹在煤层间的脉石，是成煤过程中与煤层伴生的一种含碳量低，但比煤坚硬的黑灰色岩石，是在采煤过程和洗煤过程中分离出的废渣，实际上它是由含炭物和岩石组成的混合物。据统计，我国每年煤矸石排放量近1亿t，目前已累计堆积30多亿t。煤矸石长期堆积，不仅占用大量土地，而且由于自燃和污水渗漏，造成大气和地下水的严重污染。煤矸石中含有金属有钒、钴和镓等，但含量都比较少，不具备回收条件。又因煤矸石中尚含有C、H和O，故燃烧时能产生较大的热量。通常煤矸石的发热量在4186～12560kJ/kg，显然它是一种值得开发利用的矿业废物资源。有些尚含有有害成分硫等，所以利用过程中需采取一些措施减少新的污染。 煤矸石的相关性质见表1及表2。 表1 煤矸石的化学成分/% SiO AlO FeO CaO MgO SO 烧失量 62.28 11.10 7.68 3.02 1.25 0.94 9.8 表2 煤矸石的物理性能 松散容重/(kg/m) 普氏硬度 含水率/% 塑性指数 发热量/(kJ/kg) 1198 ≦3 ≦8 ≦7.5 (1.2～1.5)×4.186 煤矸石空心砖正是综合利用煤矿废渣——煤矸石烧制的有贯穿孔洞，孔洞率15%的砖。利用煤矸石代替烧制空心砖，其发热量除满足制品本身烧成所需要的热量外，还能利用其余热干燥坯料，不仅节约了大量原煤，还节省了优质黏土和堆放矸石所占用的土地，减少对环境的污染。 1生产工艺 1.1对材料的要求 1.1.1应符合烧制空心砖对原料的要求。 由于煤矸石成因不同，各地煤矸石的化学成分差别很大，特别要严格限制原料中有害杂质的数量，尤其是CaO和SO，不能大于10%和3%。 1.1.2应具有良好的破碎加工性能。 由于煤矸石的种类不同，要求原料的布氏硬度要小于4%。 1.1.3粒径要适合。 粒径对坯体成型、干燥、焙烧都有直接影响，因为原料粒径过大，可塑性能变差，不易成型，会使挤泥机的泥缸和螺旋刀的磨损加快。粒径过细，则电耗大，为使泥条不断裂，砖坯棱角完整，焙烧后空心砖各面光滑，强度要符合要求，通常粒径应不大于1mm，其