浅谈FRP对现代竹结构的加固研究 摘要：通过数年的研究和努力，现代竹结构房屋作为一种新型环保节能建筑，在国内外开始得到关注。然而现代竹结构也存在承载力等方面的问题，因此提出了采用FRP材料加固现代竹结构的方法。本文主要介绍了现代竹结构、国内外FRP加固现状等。在现代竹结构研究中，FRP加固属于较新颖的研究领域，因此这仍是一个亟待解决的关键科学问题 关键词：现代竹结构，FRP，加固，承载力 ?Abstract: Through several years’ research and effort, modern bamboo structure housings as a new environmental-friendly and energy-saving building, getting more attention from people at home and abroad. However modern bamboo structure still have problems such as the bearing capacity , here comes the method of modern bamboo structuresstrengthened with materials. This paper mainly introduces the structure of the modern bamboo, domestic and foreign status of FRP reinforcement, etc. In the study of modern bamboo structures, FRP reinforcement come from a new research field, so it is still a key scientific problems to be solved. Keywords: modern bamboo structure ; FRP; reinforce; the bearing capacity 0引言 目前，建筑主要以钢筋混凝土结构，钢结构及砌体结构为主，这些结构需要消耗大量的钢材，水泥和粘土，本身是一种高能耗、高污染的产业，显然不符合绿色建筑的要求。迄今为止，建筑领域使用最多的天然可再生的有机材料是木材，然而我国是一个森林面积相对较少，木材资源也相对匮乏的国家，即便是人工造林，也由于林木本身的成材周期较长，可取用的资源仍然极为有限，不可能大量用于建造木结构房屋。而同样轻质高强的竹材，由于其丰富的资源和出色的繁殖生长能力，恰恰能够弥补木材资源匮乏这方面的缺陷。因此其在生态性、保温节能性、抗震性能及施工与工业化方面具有突出的优点，给我们带来绿色与环保的新概念。但是，在竹结构的研究与应用过程中发现，存在以下突出问题：（1）弹性模量低，受弯构件的刚度较小；（2）竹材抗拉强度相对较低，中性轴在截面对称轴附近，材料用量较多；（3）力学性能较离散，往往由于局部缺陷提前破坏；（4）破坏模式较脆。在基本不改变现有竹材加工工艺的情况下，利用FRP筋增强材料改善竹材受弯构件的力学性能，提高竹材对于结构工程的适用性，通过试验初步验证了FRP筋增强竹材受弯构件的有益效果。FRP筋增强竹梁CFRP筋增强试件刚度提高10%，FRP筋增强试件刚度提高5%，横截面应变沿高度方向的分布基本上呈线性，平截面假定是成立的生态性、保温节能性、抗震性能及施工与工业化方面具有突出的优点弹性模量低，受弯构件的刚度较小竹材抗拉强度相对较低，中性轴在截面对称轴附近，材料用量较多力学性能较离散，往往由于局部缺陷提前破坏破坏模式较脆在基本不改变现有竹材加工工艺的情况下，利用FRP筋增强材料改善竹材受弯构件的力学性能,蒋身学,吕清芳,等[J].建筑结构,200D].东南大学博士学位论文,2006. [4]王文炜.纤维复合材料加固钢筋混凝土梁抗弯性能研究[0].大连理工大学博士学位论文,2003. [5]Plevris N,Triantafillou T. FRP2Reinforced Wood as Structural Material [J].Journal of Materials in Civil Engineering,1992. [6]魏洋,蒋身学,李国芬. FRP筋增强竹梁的力学性能研究[J]. 工业建筑, 2009,39. [7] 单波,周泉,肖岩. 现代竹结构技术在人行天桥中的研究与应用[J]. 湖南大学学报（自然科学版）, 2009. [8]黄桂秋.竹材加固的力学性能试验研究分析[D]. 上海交通大学硕士学位论文, 2013. [9]周爱萍.重组竹受