碳材料孔控制研究进展..doc

碳材料孔控制研究进展 简要说明炭材料孔的形成、分类和描述，之后评述了控制碳材料孔结构技术的的重要性。，然后和个来说明在碳材料中孔结构控制的重要性。孔结构控制技术，包括。Abstract: Techniques for controlling the pore structure and its importance in carbon materials are reviewed after a brief explanation on formation mechanism and classification and characterization of pores. The understanding of four kinds of pore-forming processes are reviewed and then five application areas are presented to show the importance of pore structure control in carbon materials, which included VOC treatment and recycling，Water purification，gasoline vapor adsorption, CO2 capture, and carbon electrodes for electric double layer capacitors. Pore structure control techniques are shown, including the macroporous control, mesoporous control and micropore control. 活性炭是一种具有丰富内部孔隙结构、高空隙率和较高比表面积的六方晶格型碳。因活性炭性价比高、化学稳定性[1]、吸附性能热稳定性好[2]等，。对环境安全和污染控制关注的提高为活性炭吸附的应用开辟了新的领域，在很多化工厂，如印刷，涂料，纺织印染，聚合物加工。[3–6]，有文献报道，当孔隙大小为吸附分子的2～4倍时最有利于吸附，可以根据吸附质分子选择吸附性能最好的活性炭，但一般活性炭的孔径并不均一，选择性吸附效果差。因此，精确控制活性炭的孔结构在不同应用领域有很强的需求。常规活性炭主要包含小孔，小孔也被IUPAC定义为微孔，即使他们只有纳米级尺寸（小于2nm），也已经吸引了注意和努力在孔尺寸和数量的控制。在最近的一些应用上即使较大的孔，被称为中孔（2～50nm）和大孔（大于50nm）都对活性炭的功能应用起作用，例如中孔在催化净化能源储存和制备 [3–13]，大孔在重油吸附上的应用等。并且，孔的数量和尺寸、同种尺寸和形态孔也需要控制。 为满足特殊应用的特殊需求，相关学者提出很多方法和技术用于创造拥有特定孔结构的活性炭材料，控制孔的尺寸和数量。这些技术措施可分为一下三种：一是选择特殊原料实现活性炭特殊孔隙结构及孔尺寸，二是通过活性炭制作过程控制孔的尺寸和数量，形成特殊孔隙结构。三是对制作完成的活性炭用修饰或填充等措施改变活性炭原有性质实现控制孔隙结构、孔的尺寸和数量孔。这些提出的工程和技术工艺似乎可以满足在孔结构方面的需求，但是这些技术应用于工业生产还需要一些突破。 1 孔的形成机理及分类 1.1 活化法成孔机理 活化反应属于气固相系统的多相反映，活化过程括物理和化学两个过程，整个过程包括气相中的活化剂向炭化材料外表面扩散、活化剂向炭化料内表面的扩散、活化剂被炭化料内表面吸收、炭化料表面发生反应生成中间产物（表面络合物）、中间产物分解成反应产物、反应产物脱附、脱附下来的反应产物由炭化料内表面向外表面扩散等过程[14]。 1.1.1 气体活化法 物料在炭化过程中以形成了类似石墨的基本微晶结构，在微晶之间形成了初级空隙结构，不过由于这些初级孔隙结构被炭化过程中生成的一些无序的无定形碳或焦油馏出物所堵塞或封闭，因此炭化料的比表面积很小。气体活化的过程就是用活化气体与C发生氧化还原反应，侵蚀炭化物的表面，同时去除焦油类物质及未炭化物，使炭化料的微细孔隙结构发达的过程。杜比宁（Dubinin）理论认为，烧失率小于50%时，得到的是微孔活性炭；烧失率大于75%时，得到的是大孔活性炭；烧失率在50%～75%时，得到的是具有混合结构的活性炭。活化反应通过以下三个阶段最终达到活化造孔的目的。 第一阶段：开放原有的闭塞孔。即高温下，活化气体首先与无序碳原子及杂原子发生反应，将炭化时已形成但却被无序碳原子及杂原子所堵塞的孔隙打开，暴露出基本微晶表面。 第二阶段：扩大原有孔隙。在此阶段，暴露出来的基本微晶表面上的C原