苯乙烯安全贮运条件研究.doc

苯乙烯安全贮运条件研究 苗夫传，李铭慧，王海燕，崔群 （南京工业大学，南京，210009） 摘 要: 本文研究了贮存温度、阻聚剂含量、铁锈含量及贮存时间对苯乙烯贮运过程中过氧化物和聚合物生成量的影响。实验结果表明：苯乙烯聚合物和过氧化物生成量随温度的升高、贮存时间的增加、铁锈含量的增大而增加；苯乙烯的贮存温度为20-30℃，阻聚剂TBC含量为10-18mg/kg，贮存时间为8-9天，此时聚合物含量符合贮运质量指标；从而为苯乙烯安全贮存及运输提供有价值的基础数据。 关键词: 苯乙烯; 聚合; 阻聚剂; 贮运; 安全 STUDY ON CONDITIONS OF SYYRENE STORAGE AND TRANAPORTATION MIAO Fuchuan, LI Minghui, WANG Haiyan, CUI Qun ( Nanjing University of Technology, Nanjing , 210009 ) Abstract: This paper investigates relations between storing temperature, inhibitor content, amount of rust , storing time and polymer, peroxide on styrene’s safe storage and transportation. It indicates that polymer and peroxide increase with increasing of storing temperature, storing time and amount of rust. When styrene is stored for 8 or 9 days with inhibitor(TBC) concentration of 10-18mg/kg at 20-30℃, polymer added is consistent with guideline of quality about styrene. Therefore it can provide useful basic data for safe storage and transportation of styrene. Keywords: styrene; polymerization; inhibitor; storage-transportation; safety 0 引言 苯乙烯是合成高分子材料的重要原料之一，也是石油化工的基础产品，在生产和生活中有着广泛的应用。苯乙烯单体中存在不饱和双键，常温下极易发生聚合反应，在贮运过程中容易出现管道堵塞及影响产品质量等问题[1-4]。目前工业生产上苯乙烯的贮存温度一般为18-20℃，运输过程中的温度为常温，但在夏天，由于环境温度较高，聚合极易发生，因而，适宜的贮存温度及相关条件的确定成为苯乙烯安全生产及运输过程中必须解决的问题。当前国内关于苯乙烯安全贮运条件方面的研究文献报导甚少。为此，本文研究了贮存温度、时间、铁锈含量和阻聚剂含量对苯乙烯安全贮运的影响，得到苯乙烯安全贮运较适宜的条件，从而为苯乙烯的安全贮运提供有价值的基础数据。 1 实验部分 1.1试剂与仪器 试剂：正己烷、无水甲醇、苯乙烯、异丙醇、乙酸、盐酸羟胺、甲醇、硫代硫酸钠、碘化钠等为分析纯，阻聚剂TBC（对叔丁基邻二苯酚），原料样A、原料样B、原料样C都来自扬子石化贮运厂，它们的具体质量参数如表1。 Table1 Main guideline of quality about styrene 质量指标 A实测值 B实测值 C实测值 聚合物含量,mg/kg 总醛含量,mg/kg 过氧化物含量,mg/kg 色度,APHA 纯度,% 阻聚剂(TBC)含量, mg/kg ≤10 ≤50 ≤100 ≤10 ≥99.7 ≥9 1.0 16.4 5.13 5 99.85 17 1.0 19.6 8 10 99.87 14.2 1.0 48 8 10 99.8 13.8 仪器：分光光度计722s，低温恒温槽DCW-3506，数显恒温水浴锅HH-2，分析天平FA2104，旋片真空泵ZXZ-1，套式电热器DWK。 1.2 实验方法 1.2.1苯乙烯试样的处理 苯乙烯原料样中含有一定量的阻聚剂TBC，在实验前首先要进行处理。方法是用20g/L的氢氧化钠溶液洗涤3次，然后用蒸馏水洗涤3次。并现处理现用。 1.2.2 苯乙烯贮存实验 在三口烧瓶中装入一定量的苯乙烯试样，并按要求加入阻聚剂和铁锈，用橡胶塞塞住三口瓶，其中两边的口用带玻璃直通阀的橡胶塞塞住，然后把抽真空装置连接