loctite fixmaster steel liquid汉高乐泰fixmaste.PDF

Technical Data Sheet LOCTITE? Fixmaster? Steel Liquid May-2013 PRODUCT DESCRIPTION LOCTITE? Fixmaster? Steel Liquid provides the following product characteristics: Technology Epoxy Appearance (Resin) Grey LiquidLMS Appearance (Hardener) Blue liquidLMS Appearance (Mixed) GreyLMS Components Two components - requires mixing Mix Ratio, by volume - 4 : 1 Resin : Hardener Mix Ratio, by weight - 9.5 : 1 Resin : Hardener Cure Room temperature cure Application Bonding Specific Benefit ● Castable liquid - repairs hard to reach areas ● Rebuilds worn parts fast - limits downtime ● High steel content - cures to a metal-like finish ● Superior adhesion - bonds well to all metal substrates LOCTITE? Fixmaster? Steel Liquid is a two-part steel filled pourable epoxy repair material. It has high compressive strength and can be machined, drilled, tapped or filed just like steel. Applications include casting metal parts and pouring molds, parts and fixtures. This product is typically used in applications with an operating range of -30 °C to 110 °C (-20F to 225F). Mixed: Density @ 23 °C, g/cm3 Coverage 1.8 213 cm3 per 0.45 kg (13 in3 per 1 lb) TYPICAL CURING PERFORMANCE Curing Properties Cure Time @ 25 °C, hours Gel Time @ 25 °C, minutes Working life, minutes 6 30 to 40LMS 25 Cure Speed vs. Temperature The graph below shows the shear strength developed with time on grit blasted steel lap shears at different temperatures and tested according to ISO 4587. 125 45 °C 100 % of Full Strength at 22°C 75 35 °C 50 25 °C 25 15 °C 5 °C 0 0 2 4 6 8 12 16 20 24 Time, hours TYPICAL PROPERTIES OF UNCURED MATERIAL Resin: Weight per volume kg/L 2.24 to 2.33 (lbs/gal) (18.7 to 19.4LMS) Viscosity, Brookfield - RV, 25 °C, mPa·s (cP): Spindle 7, speed 20 rpm, 70,000 to 85,000LMS Flash Point - See MSDS Hardener: Weight per volume kg/L (lbs/gal) 0.96 to 0.984 (8.0 to 8.2LMS) Viscosity, Brookfield - RV, 25 °C, mPa·s (cP): Spindle 2, speed 50 rpm, 250 to 350LMS Flash Point - See MSDS TYPICAL PROPERTIES OF CURED M