优化6m焦炉配煤方案.doc

优化6m焦炉配煤方案，提高焦炭质量 齐 婳，李德瑾，纪同森，王华兰，彭新华 （济南钢铁集团总公司，山东 济南 250101） 摘　要：济钢的两座6m焦炉投产初期焦炭强度波动，为此，以20kg小焦炉试验、岩相检测、焦炭反应性和反应后强度检测为主要试验手段，对新汶、官庄、圣佛、阳泉曲、新坡、两度、卜村等10多个煤种作了70余炉配煤炼焦试验，优化了配煤，完善了6m焦炉的用煤结构。 关键词：6m焦炉；配煤方案；小焦炉试验；焦炭质量 中图分类号：TQ522.16　　 文献标识码：A　　 文章编号：1004-4620（2006）04-0037-03 Optimizing Blending Plan of 6m Coke Oven for Improving the Coke’s Quality QI Hua, LI De-jin, JI Tong-sen, WANG Hua-lan, PENG Xin-hua （Jinan Iron and Steel Group General Company, Jinan 250101, China） Abstract：At the beginning of 6m coke oven starting-up, the coke’s quality was not steady. Therefore, more than 70 times of coking test for blend were finished with many coal ranks such as Xinwen coal, Guanzhuang coal, Shengfu coal, Yangquanqu coal Xinpo coal, Liangdu coal, Pucun coal etc. by 20kg test oven, petrographic examination and using CRI and CSR examination as main means. The blending plan was optimized and the coke’s quality was improved. Key words：6m coke oven; blending plan; test oven experiment; coke’s quality 　　为了弥补焦炭需求缺口，济南钢铁集团总公司（简称济钢）分别于2005年3月和4月投产了两座6m焦炉。由于济钢对6m焦炉入炉煤质量要求缺乏生产经验，在投产初期，6m炉焦炭抗碎耐磨强度波动无规律，相邻班差几个百分点，质量有失控状态。因为煤源的差异，操作水平的不同，其他厂家的情况也不能照搬。2005年6～9月，济钢技术中心和焦化厂联合以煤焦实验室的20kg小焦炉试验、岩相检测及焦炭反应性和反应后强度检测等为主要试验手段，对新汶、官庄、圣佛、阳泉曲、新坡、两度、卜村等10多个煤种进行了70余炉配煤炼焦试验，优化了配煤，完善了6m焦炉的用煤结构。 1 主要试验设备 　　（1）20kg试验焦炉：为电加热（硅钼棒）、炉顶直接装煤、单炉门底开式焦炉，炭化室由4块高铝整砖镶砌而成。焦炉长宽高分别为400、200、400mm；容积0.032m3。装煤量为干煤23kg；装煤水分（10±1）%；炭化室平均温度（1080±5）℃；焦饼中心温度不小于950℃；结焦时间8h。　　（2）HY-4岩相自动测试设备：HY-4型全自动显微镜光度计10min可测定一个样品；测定过程中可自动调节显微镜焦距，保证测定数据真实可靠；可按要求自动旋转显微镜偏光镜，测定焦炭、中间相、矿物等各相异性物质的有关参数；可根据测定对象的反射率变化范围，由计算机软件确定合适的仪器放大倍数与自动校正仪器零点；充分利用仪器的量程与分辨率；采用“多点提取”镜质组、曲线相减消除粘结物等数据处理技术，由反射率自动测定结果确定其它有关参数。　　（3）焦炭反应性、反应后强度测试设备：由安徽工业大学按照国标GB/T4000-1996焦炭反应性及反应后强度试验方法的标准制作，确保了试验的精密度。 2 试验用煤种 　　试验用煤种主要为济钢焦化厂现用煤种，均是卸车过程中取样，其工业分析数据和岩相组分分别见表1和图1。 表1 试验用煤种的工业分析数据 矿点Ad/%St/%Vd/%GY/mm新汶8.050.8035.799015.5官庄8.510.4134.018516.0圣佛10.210.9432.28828.0阳泉曲8.391.6128.919431.0胡屯8.501.4637.849225.0新坡10.730.8321.390