1004 环保型免退火33B2冷镦钢盘条的研发.pdf

2016 年（第十九届）全国炼钢学术会议论文集 环保型免退火33B2 冷镦钢盘条的研发 李永超 阮士朋 郭明仪 （邢台钢铁有限责任公司, 河北 邢台054027 ） 摘 要：33B2 冷镦钢常用于生产 8.8 级高强度紧固件。本文介绍了邢钢 33B2 冷镦钢的成分设计、生产工艺和组织性能。通 过采用铁水预脱硫-80tBOF-80tLF -4 流 325mm×280mm 方坯连铸机-开坯-修磨- 高速线材轧制流程开发了环保型免退火 33B2 。各项性能检验均满足用户要求，并为用户减省软化退火工序及降低生产成本。 关键词：33B2 盘条；免退火；冷镦钢；生产过程；工艺控制 Development of environmental and non-annealed 33B2 cold heading steel wire rod Li Yongchao ，Ruan Shipeng ，Guo Mingyi （Xing tai Iron and Steel Co. ，Ltd Hebei Xingtai 054027,.China ） Abstract ：33B2 cold heading steel is usually used to produce 8.8 high strength fasteners. The composition design ,production process and microstructure property of 33B2 are introduced in this paper. The environmental and non-annealed 33B2 cold heading steel was produced by 80t BOF-80tLF refining -4 strand 325mm×280mm billet caster--blooming-grinding-high speed wire rolling. The results of performance test showed that the 33B2 can meet customer demand ,save soft annealing process and reduce cost for customer. Key words: 33B2 wire rod; non-annealed; cold heading steel; production process; process control. 1 前言 [1-2] 冷镦钢线材主要用于制造螺栓、螺母等紧固件和一些冷镦成型的零部件，用途广泛 。33B2 属于中 碳含硼冷镦钢，欧标冷镦钢牌号，常用于生产欧系乘用车用 8.8 级及以上高强度紧固件。目前各标准厂家 在生产 8.8 级及以上紧固件前通常采用酸洗、拉拔、球化退火（或软化退火）等工序，其中退火工序成本 [3-4] 高，污染环境，且造成线材表面脱碳严重 。因此从节约能源、降低用户生产成本角度出发，开发了环 保型免退火33B2 冷镦钢。 2 化学成分设计 为保证33B2 具有良好的冷镦性能、淬透性能及免退火要求，对33B2 化学成分进行了设计，见表1所 示。 表1 33B2 钢的化学成分设计（%） Table 1 Chemical composition design of 33B2 C Si Mn S P B Alt 用户要求 0.30-0