含碳耐火材料抗氧化涂料的现状与发展趋势.pdfVIP

炉用材料 《工业加热》第34 卷2005 年第4 期 含碳耐火材料抗氧化涂料的现状与发展趋势 欧阳德刚 （武汉钢铁集团公司 武钢技术中心工艺研究所，湖北 武汉 430080） 摘要：介绍了含碳耐火材料实际应用中氧化造成的危害，根据国内外对防止氧化表面涂层技术的研究状况，对涂料的防止氧化作用 机理、性能要求与组成成分进行了分析。目前开发的抗氧化涂料品种较少，有必要在涂料品种与涂层的综合性能提高方面进一步开 展工作。 关键词：含碳耐火材料；抗氧化性；涂料 中图分类号： 文献标识码： 文章编号： ( ) TQ 175.7 14 A 1002-1639 2005 04-005 1-04 Present Status and Development of Anti-oxidation Coatings for Carbon-containing Refractory OUYANG De-gang （ ， ） Wuhan Iron Steel Group Corp., Wuhan 430080 China Abstract ：The harms caused by oxidation during carbon-containing refractory using were introduced. Based on the research current situation of surface coatings technology for anti-oxidation over the world, the anti-oxidation mechanism, properties demanding and component of the coatings were analyzed. The varieties of anti-oxidation coatings been developed were fewer, the more research works were done necessarily on the varieties of anti-oxidation coatings and advancing the integrated performances of coatings. Key words：carbon-containing refractory ；anti-oxidation ；coating 用，但一般限用于1 000 ℃以下的氧化防护1 。添加抗氧 1 前 言 化剂方法是在含碳耐火材料中添加适量的抗氧化剂，如 含碳耐火材料由于石墨的引入提高了耐火材料的抗 Al 、Si、Mg、SiC、B C 等，其作用原理有二：其一是利 4 渣性能和抗热震稳定性能，因而被广泛地应用于冶金炉 用抗氧化剂或者抗氧化剂和碳的反应物与氧的反应亲和 窑热工设备的内衬上。然而，由于耐火材料中碳质材料 力大于碳与氧的反应亲和力的性能，使其先于碳被氧化 容易被氧化，导致耐火砖结构疏松，使含碳耐火材料优 而使含碳耐火材料中的碳得到保护；其二是利用抗氧化 良使用性能的发挥受到抑制