与耐蚀铸造合金相类似的锻造合金牌号.doc

与耐蚀铸造合金相类似的锻造合金牌号(铸件-锻件材料牌号对照)?? 2010-11-26 16:40:33|??分类： 默认分类 |??标签： |字号大中小?订阅 铸造合金 UNS 锻造合金 UNS CA6NM J91540 CA15 J91150 410 S41000 CA15M J91151 CA40 J91153 420 S42000 CB30 J91803 431 S44200 CB7Cu1 J92180 17-4/630 S17400 CB7Cu2 J92110 15-5/XM-12 S15500 CC50 J92615 446 S44600 CD4MCu J93370 255/F61 S32550 CD7MCuN 255/F61 S32550 CE30 J93423 CF3 J92500 F304L S30403 CF3M J92800 F316L S31603 CF3MN F316LN S31653 CF8 J92600 F304 S30400 CF8C J92710 F347 S34700 CF8M J92900 F316 S31600 CF10SMnN Nitronic 60 S21800 CF16F J92701 303 S30300 CF20 J92602 302 S30200 CG6MMN J93790 Nitronic 50/FXM-19 S20910 CG8M J93000 F317 S31700 CH20 J93402 309 S30900 CK3MCuN J93254 254SMO/F44 S31254 CK20 J94202 F310 S31000 CN3MN AL6XN/F62 N08367 CN7M N08007 Alloy 20/20Cb-3 N08020 CN7MS J94650 CW2M N26455 Hastelloy C4 N06455 CW6M N30107 CW6MC N26625 Inconel 625 N06625 CW12MW N30002 Hastelloy C N10002 CW12MW N30002 Hastelloy C276 N10276 CX2MW N26022 Hastelloy C22 N06022 CY5SnBiM N26055 CY40 N06040 Inconel 600 N06600 CZ100 N02100 200 N02200 M25S N24025 M30C N24130 Monel 400 N04400 M30H N24030 M35-1 N24135 Monel 400 N04400 M35-2 N04020 Monel 400 N04400 N7M N30007 Hastelloy B2 N10665 N3M N30003 Hastelloy B2 N10665 N12MV N30012 Hastelloy B N10001 CD3MN/4A J92205 2205/F51 S31803 CU5MCuC N08826 Incoloy 825 N08825 CD3MWCuN J93380 Zeron 100/F55 S32760 ASTM制定和出版了三份有关耐蚀合金的技术规范，两份是关于不锈钢和其它耐蚀高合金钢铸件，A743／743M 和A744／744M，另一份是关于镍基铸件，A494／494M。A743 用于一般性腐蚀设备，A744 用于腐蚀性严重的设备：A744 除较小的维修外，均需要进行焊后热处理；A743 不需要。对于A494，如果需要进行焊后热处理，用户需要说明。 ASTM A743：通用铸件，铁-铬，铁-铬-镍，镍基，耐腐蚀。ASTM A744：恶劣条件下用的铸件，铁-铬，镍基，耐腐蚀。这两种规范都要求对铸件进行固溶退火处理，以便大部分去除铸件内的合金偏析和树枝状组织，特别是大断面铸件。根据合金情况，1040℃或更高温度的高温退火，可使化学成分和显微组织更加均匀，并可溶解碳化物。退火后，铸件具有最佳的耐腐蚀状态。由于钼在铸件中偏析严重，为了使钼的分布更加均匀，以获得最佳耐腐蚀性能，含钼钢种的退火温度需要1095～1120，广泛使用的CF3M 和CF8M 必须在1120的温度，而不是规范所要求的最低1040温度退火。 不锈钢铸件通常由加工厂进行组装焊接或在使用过程中进行补焊，或在铸造厂对缺陷进行补焊。当在腐蚀严重的环境中使用铸件时，选择低碳钢种，例如CF3 或CF3M 就可避免焊缝热影响区内形成的碳化铬所造成的问题。在锻造合金中所论述的碳化铬对晶间腐蚀的影响也适用于铸造合金。