学兔兔 2014年第2期 混凝土与水泥制品 2014 No．2 2月 CHINA CONCRETE AND CEMENT PRODUCTS February 玻化微珠保温混凝土中减水剂的复配研究 曹铭真，李 珠，赵 林，张 玉 (太原理工大学建筑与土木工程学院，030024) 摘 要：对泵送玻化微殊保温混凝土的坍落度损失问题及解决方案进行了分析．通过在减水剂中掺入不同量引 气剂和缓凝剂进行了玻化微珠保温混凝土坍落度损失试验．并确定了最优掺量。试验结果表明，引气剂最佳掺量为 2‰，缓凝剂为2％。该掺量下坍落度为255mm；lh坍落度损失为15rnm；28d抗压强度为35．9MPa。解决了玻化微珠 保温混凝土泵送过程中的坍落度损失问题和凝结时间问题 关键词：引气剂；缓凝剂；玻化微珠保温混凝土：坍落度 Abstract：In order to apply the glazed hollow bead insulation concrete to the engineering better，its slump loss pmb— lem and the related solution are studied．The slump test of the concrete is carried out by mixing the air—entraining agent and retarder in the water reducer．and the optimal dosages of addition agents are determined．The result indicates tIlat the optimal dosages of the air—entraining agent and retarder are respectively 2％0 and 2％．Using the optimal mix proportion． the slump of the concrete can reach 255mm，and its slump loss is 15mm after lh，the 28d compressive strength of the con— crete is 35．9MPa，which solves the problems of the slump loss and the setting time during the pumping construction pro- Key wor~：Air—entraining agent；Retarder；Glazed hollow bead insulation concrete；Slump 中图分类号：TU528．2 文献标识码：A 文章编号：1000—4637(2014)02—68—04 0 前言 泵送混凝土对坍落度及其损失要求很高，为提 目前，我国的建筑能耗在全国总能耗中占有很 高混凝土坍落度．减少坍落度损失和延长凝结时 大比例(30％以上)。随着我国城市化进程的加快，建 间。本文进行了减水剂复配研究。在抗离析性能研 筑耗能问题将越来越突出，节能减排已成为全社会 究的基础上，对混凝土坍落度和抗压强度影响因素 关注的问题。降低建筑能耗、推进建筑节能是我国 进行了分析，初步确定了可改善混凝土坍落度的因