甘肃某难选红柱石矿选矿试验研究.pdfVIP

第 卷第 期 37 5 Vol.37 No.5 非金属矿 2014年9月  Non-Metallic Mines September, 2014 甘肃某难选红柱石矿选矿试验研究 金俊勋  高惠民  冯晓菲  杨慧群  管俊芳  张凌燕 （武汉理工大学资源与环境工程学院，湖北 武汉 430070） 摘  要  对甘肃某难选红柱石矿采用选择性磨矿- 脱泥- 磁选- 浮选工艺进行选矿试验研究，探索了选择性磨矿、脱泥、磁选、浮选的适宜工 艺条件。采用红柱石含量为10% 的原矿，通过磁选- 浮选工艺流程，最终获得红柱石含量87.78%，回收率50.61% 的红柱石精矿。 关键词  红柱石；浮选；磁选；脱泥 TD973 A 1000-8098(2014)05-0040-03 中图分类号： 文献标识码： 文章编号： Mineral Processing of a Refractory Andalusite Ore in Gansu Jin Junxun Gao Huimin Feng Xiaofei Yang Huiqun Guan Junfang Zhang Lingyan (School of Resources and Environment Engineering, Wuhan University of Technology, Wuhan, Hubei 430070) Abstract The low grade andalusite mine from Gansu was separated by flow of selective grinding, desliming, magnetic separation and flotation process. The best technological conditions of selective grinding, desliming, magnetic separation and flotation were researched. As for the ore in which the content of andalusite is 10%, by the joint process of magnetic separation and fltation, good beneficiation indexes were obtained. Key words andalusite; flotation; magnetic separation; desliming 红柱石为蓝晶石族高铝矿物，化学成分为 图谱分析可知，试样主要矿物组成(w/%) 为：红柱石， Al SiO 。红柱石属于斜方晶系，摩氏硬度为6.5~7.5 ， 10；石英，35 ；白云母+ 黑云母，40 ；钠长石，10；磁铁 2 5 相对密度约为3.1~3.2 [1-2] 。红柱石有很高的熔融点 矿，2 ；褐铁矿，1；其它，2 。 和良好的耐火性能，在常压下加热至1400 ℃左右，红 1.3 试剂 硫酸，分析纯；石油磺酸钠，工业纯；水玻 柱石开始重结晶为莫来石。莫来石具有耐高温、热膨 璃，工业纯，十二胺，分析纯。 胀低、耐磨损性、耐化学腐蚀性等良好特性。因此，红 1.4 仪器设备 锥形球磨机，XMQ-240×90 ；高