脂肪族减水剂的合成及其与聚羧酸减水剂复配研究.pdf

40 脂肪族减水剂的合成及其与聚羧酸减水剂复配研究 刘才林 脂肪族减水剂的合成及其与聚羧酸减水剂复配研究 刘才林，任先艳 西南科技大学 材料科学与工程学院，四川 绵阳 6200 F A S 摘要：以甲醛( )、丙酮( )、磺化剂( )为主要原料，合成了脂肪族减水剂，系统研究了反应原料用量与磺化剂 种类对脂肪族减水剂分散性能的影响，并对自制的脂肪族减水剂结构进行了红外光谱表征。通过脂肪族减水剂 与聚羧酸减水剂的复配研究，提高这两类减水剂的应用潜力。 关键词：脂肪族减水剂； 混凝土外加剂； 合成； 复配 TU528.042 B 004-672(2009)0-0040-03 中图分类号： 文献标识码： 文章编号： Study of Synthesis of Aliphatic Water Reducer and Its Compounding with Polycarboxylic Water Reducer / Liu Cai-lin et al // Southwest University of Science and Technology Abstract: Aliphatic water reducer was synthesized with formaldehyde(F), acetone(A), and sulfonating agent(S) as main raw materials. Effects of content of reactants and species of sulfonating agents on dispersion of aliphatic water reducer were systematically studied and structure of self-made aliphatic water reducer was characterized by IR. Through study of compounding of aliphatic water reducer and polycarboxylic water reducer , applied potential of both water reducers were improved. Key Words: aliphatic water reducer; concrete admixture; synthesis; compounding 1.2 随着混凝土技术的发展，高效减水剂已经成 脂肪族减水剂的合成 为混凝土外加剂中最重要的组成部分。目前国内的 将全计量的甲醛与磺化剂加入带有回流装置的 外加剂市场中，高效减水剂主要仍以萘系、聚羧酸 三颈瓶中，搅拌至溶液澄清后取出待用。将一定量 为主。然而，萘系减水剂受其结构制约，无法从根 的氢氧化钠及全计量的丙酮加入三颈瓶中，搅拌并 本上改善混凝土保坍性能；聚羧酸减水剂虽保坍性 滴加上述溶液，滴加过程中温度不大于56℃。滴加 能优异，与水泥适应性好，但因价格昂贵，其应用 结束后升温至90℃并保温，测净浆流动度达到目标 范围受到一定的限制。脂肪族高效减水剂具有掺量 值后停止反应。 1% 1.3 低、硫酸钠含量少(小于 )、冬天无结晶、对钢筋 脂肪族减水剂的应用性能研究