简便合成超微锡氧化物纳米颗粒嵌入碳作为锂离子电池的高性能阳极.doc

Facile synthesis of ultrasmall tin oxide nanoparticles embedded in carbon as high-performance anode for lithium-ion batteries. 简便合成超微锡氧化物纳米颗粒嵌入碳作为锂离子电池的高性能阳极 Introduction its high theoretical capacity, low toxicity, high abundance and safe working potential . 它具有高理论容量，低毒性，高丰度和安全工作的潜在 It also suffer from the drawbacks of the huge volume change and low electronic conductivity during lithiation/delithiation processes. 它也受到在锂化/脱锂过程中巨大的体积变化和电子电导率低的缺点。 Herein, the ecperiment have prepared a SnO2/C composite of ultrasmall SnO2 nanoparticles (~6 nm and ~59.4% by weight) embedded in carbon matrix (denoted as SnO2/C-59) by a facile hydrothermal and subsequent carbonization approach. 在此，实验通过一种简便的水及后续碳化方法制备了超微型的SnO2纳米粒子（?6 nm和?重量的59.4％），嵌在碳基体的二氧化锡/碳复合材料（表示为二氧化锡/ C-59），。 Experimental section 2.1. Preparation of samples 0.35克锡酸钠的?4H2O和1.2克的D-葡萄糖溶解于 14毫升去离子水，并搅拌1小时。然后将溶液 转移至25 mL的聚四氟乙烯内衬的不锈钢高压釜中， 冷却前密封，并保持在180°℃下的烘箱中8小时 室温。然后，将产物离心收获 并用去离子水和乙醇。所制备的前体随后在温度 500度下被碳化3小时，在氩气保护气氛下温度每分钟递减0.5度。。最后，获得二氧化锡/ C-59复合材料 。 2.2.SnO2/C-59的均匀分布，和碳基质的电导率，它可以有效地解决粉碎的电接触，并且在循环过程中粒子的凝集损失的问题的电子传导性，因此有助于优异的锂存储和循环稳定性。这使得合成SnO2/C-59复合材料作为锂离子电池阳极材料有很好的前途。