矿渣粉颗粒群参数对矿渣活性和混合水泥性能地影响.pdf

- 10 - 2010.No.2 矿渣粉颗粒群参数对矿渣活性和混合水泥性能的影响 肖忠明，何 力，郭俊萍，程 伟，席劲松，任丽云，李文武，宋立春 （中国建筑材料科学研究总院，北京 100024） 摘要：以混合材料的填充效应和微集料效应为基础，测试了不同颗粒分布矿渣粉制备的水泥的物理性能，研究了矿渣 粉颗粒群参数对水泥使用性能和混合水泥抗压强度比的影响。 结果表明，矿渣粉颗粒分布宽、粗大化有利于混合水泥 使用性能的提高；同时，颗粒堆积密度也影响混合水泥抗压强度比的高低，但主要对早期作用明显，而后期的抗压强度 比则与矿渣粉的比表面积直接相关。 关键词：矿渣粉；颗粒群参数；水泥性能；活性 Abstract: Based on filling effect and micro-aggregate effect of admixtures, the physical properties of cement prepared by GGBFS with different particle size distribution were tested, and the effect of slag particle group parameters on cement service performance and compressive strength ratio of blended cement was studied. The result showed that the wide distribution and coarse particle size of GGBFS was helpful to improve cement service performance. At the same time, the accumulation density of particles influenced the compressive strength ratio of blended cement especially at the early age, while the compressive strength ratio at later age was correlated to specific area of GGBFS. Key words: GGBFS; particle parameter; cement properties; activity First authors address: China Building Materials Academy, Beijing 100024, China 中图分类号： 文献标识码： 文章编号： （ ） TQ172.718 A 1002－9877 2010 02-0010-05 0 引言 利用矿渣粗粉、矿渣粉和矿渣微粉配置的混合矿 渣粉的颗粒群参数见表 和表 。 颗粒群参数中，筛 随着粉磨技术以及混凝土技术的发展，矿渣微粉 2 3 已成为水泥和混凝土的重要组成部分。为了规范矿渣 余按GB/T1345—2005 进行，比表面积按GB/T8074— 微粉的生产和使用，我国制定了《用于水泥和混凝土 2008 进行， 颗粒分布由 MASTERSIZER 激光颗粒仪 中的粒化高炉矿渣粉》 国家标准。 测定，介质为无水乙醇。 混合水泥颗粒参数根据配料