热轧钢板表面翘皮及线形条纹缺陷检测.pdf

2004 年第 6 期 　　　　　　　　　　　　　　　　　物 　理 　测 　试 　　　　　　　　　　　 3 1 热轧钢板表面翘皮及线形条纹缺陷检测 袁方明 , 　刘秀梅 , 　王新华 (北京科技大学冶金学院 , 北京 100083) 摘 　要 :通过对鞍钢热轧钢板表面翘皮和线形条纹缺陷的研究 ,认为此类缺陷是铸坯表层气泡造成 的。对该类缺陷的成因进行了分析和推理 ,认为是铸坯表层气泡在轧制延伸过程中造成钢板分层 并在表层逸出导致开裂形成翘皮 。大多数情况下 ,这种分层在随后的轧制过程中被压合 ,而线形条 纹则是翘皮被压合后形成的两条边界 。 关键词 :热轧 ;钢板 ; 翘皮 ; 线形缺陷 Detection of Surface Upwarping and Line Defects f or Hot Rolled Plates YUAN Fangming , 　L IU Xiumei , 　WAN G Xinhua (University of Science and Technology Beijing , Beijing 100083 , China) Abstract : The detection of surface upwarping and line defect s for hot rolled plates produced by Anshan Steel was made . These defect s was ascribed to t he bled of slab surface . When t he bled of t he slab surface are extended during rolling , t he slab surface is delaminated and form t he surface upwarping when t he gas in t he bled escap e along t he gap of delamination . Commonly , t his kind of delamination will be impressed well during hot rolling , and t he line defect s become t he boundaries of t he impressed delamination . Key words : hot rolling ; plate ; surface upwarping ; line defect 表 1 　试样的工艺参数 1 　前 　言 试样大小 厚度 试样号 卷号 钢质 备注 　　热轧和冷轧钢板的表面缺陷是影响成品合格率 mm ×mm mm 的常见问题 ,也是质量异议的重点问题之一 。其中 , 1 D381M0 1050 SPHC 180 ×200 2 5 上表面 热轧钢板 ,尤其是 2～3 mm 规格的钢板表面翘皮和 2 D381M0 1060 SPHC 4 10 ×170 2 5 上表面 线形条纹出现频率相对较高 ,并且对这两种缺陷的 成因说法不一 。为减少此类缺陷的产生 ,有必要