浅谈水性防腐涂料常见缺陷的防治.pdf

重点报道 ‖Highlight Report 浅谈水性防腐涂料常见缺陷的防治 杨惠忠 （ 无锡太湖防腐材料有限公司，江苏无锡 214161） 摘要： 水性工业涂料由于其表面张力高，容易产生诸多缺陷，作者建议采取以下方法加以防治：一是从配方源头上着手， 降低涂料的表面张力，确保有良好的附着力；二是生产工艺要把好“ 细度、pH 、黏度”这三关；三是合理的涂装管理和工艺； 四是必须要选择耐水性能良好的防锈基料、高效的防锈颜料和合适的防锈助剂。 关键词： 水性涂料； 防腐涂料； 缺陷 中图分类号： 文献标志码： 文章编号： （ ） TQ633 B 1007-9548 2016 02-0004-03 Discussion on Control Common Defects for Waterborne Anticorrosive Coatings YANG Hui-zhong (Wuxi Taihu Anticorrosive Material Co., Ltd., Wuxi 214161, Jiangsu, China) Abstract: Because the waterborne industrial coating has high surface tension, it can produce many defects in painting process. The author recommends the following methods to control the defects. Firstly, reducing the surface tension and improving adhesion of coatings from formula. Secondly, we must strictly control fineness, pH and viscosity of coating in production process. Thirdly, we will draft reasonable coating management and process. Finally, we must select anti -rust material with good water resistance, suitable pigment and anti-rust agent. Key words: waterborne coatings; anticorrosive coatings; defect 0 引言 商机，使水性技术研发有了依据。 2015 年以来，水性漆 水性防腐涂料的研发始于 世纪 年代， 由于 用树脂、颜料、助剂空前出现，不少溶剂型涂料企业忙 20 80 众所周知的原因，水性防腐涂料处于缓慢研发、小量应 起了“ 油改水”热潮，一些乳胶漆厂开始转向水性漆，有 用、性能普通的状态，步履蹒跚地走过了30 年。 的涂装企业也越来越青睐水性漆。 自此，我国水性工业 2014 年以来， 国家相关部门发布了一系列文件， 涂