二硅化钼与石英烧结后性能测试.doc

课程设计(论文) 课程名称 题 目 学 院 院 （系） 专业班级 姓 名 学 号 指导教师 年 月 日Ar气氛下MoSi2/SiO2复合材料的制备及抗压强度测试 燕咪 （，西安710005） 摘要 关 键 词： The Preparation of MoSi2/SiO2 Composite Material and The test of it’s compression strength MiYan (Xi’an university of Architecture And Technology, Faculty of materials and minerals, Xi’an Shanxi 710005) Abstract MoSi2 is a kind of Mo’s chemical compound.It has the properties of ceramics and metals,and is used in wide application.But it’s application is limited because of its low strength in high temperature and low brittleness in room temperature.So we made MoSi2 in combination with quartz to increase MoSi2’s strength in high temperature.In this paper,we mainly introduce some kinds of the preparation methods of MoSi2’s compound materials and methods and conclusions of this experiment.This experiment proved that MoSi2/SiO2 compound materials’ compressive strength is markedly exceed pure MoSi2. Key words：,SiO2,Compound material,PreperationWord,Compressive strength. 目录 绪论 4 1制备方法简述 4 1.1放电等离子烧结技术 5 1.2机械合金化 5 1.3热压法 6 1.4化学渗透法 7 2实验方法及步骤 8 2.1实验原料 8 2.2实验步骤及试样表征 8 2.3结果与讨论 9 3.结论 9 致谢 10 参考文献： 0  绪论 二硅化钼（MoSi2）是一种钼的硅化合物，由于两种院子的半径相差不大，电负性比较接近，所以其具有近似于金属与陶瓷的性质。熔点高达2030，具有导电性，在高温下表面能形成二氧化硅钝化层以阻止进一步氧化，其外观为灰色金属色泽，源于其四方α-型晶体结构，也存在六角形但不稳定的β-改性晶体结构。二硅化钼最为结构材料用于航空、汽车燃气涡轮机的高温部件、气体燃烧器、喷管、高温过滤器以及火花塞而成为金属间化合物结构材料研究的必威体育精装版热点。在这方面应用的最大障碍是其室温脆性大和高温强度低。因此二硅化钼低温增韧和高温补强是其作为结构材料实用化的关键技术。 金属间化合物MoSi2以其高熔点(2030)、高的使用温度(1600 )、优异的高温抗氧化性和耐蚀性、适中的密度(6.24g/cm3)、良好的导热性和导电性,成为高温结构用金属间化合物领域研究的必威体育精装版热点[1,2]。但是,由于MoSi2在1000以下具有较大的脆性 , 高温强度不够,特别是抗蠕变能力低而限制了它作为高温结构材料的应用。对MoSi2的室温增韧和高温补强的主要途径是用不同制备工艺引入增强体的复合化和加入其他组元的合金化。材料的制备工艺直接影响其组织与性能,因此MoSi2基复合材料的制备工艺是研究的热点。 MoSi2及其复合材料的制备方法主要有:热压(HP)、热等静压(HIP)、机械合金化(MA)、自蔓延高温合成(SHS)、熔渗、放热弥散(XDTM)和等离子喷射沉积(PS)。其中,热压是目前采用最多的成形工艺,但是由于不制备复杂形状制品而受到限制。随着复合材料制备技术的迅速发展,最近几年又出现了放电等离子烧结、微波烧结和先驱体转化法等新工艺,并且自蔓延高温合成、机械合金化和熔渗工艺的研究也有了新的进展。 1制备方法简述 由于硅化物的高熔点和室温脆性，使它的制备和性能测试有很困难，到目前为止还没有一个完整的结构硅化物及其复合材料的生产规范。但自1906年硅化物发现以来，人们已经开发出多种制备方法。 1. 放电等离子烧结(S