345-paper-B3-T250无钴马氏体时效钢研制.docVIP

编号：B3（中文全文）mechanical property and establishs the optimum heat treatment procedure.The result shows that the steel has a higher performance of hardening and toughening.We may choose 820-920℃ as the temperature of softening and solution.The change of solution temperature influences slightly the mechanics performances.It has better plasticity, toughness and cold processing in the solution condition.It has the optimum hardening and toughening when it is aged at the temperature of 480-510℃ and the insulation work of 3-8 hours.We ought to keep T250 higher purity in order to guarantee higher plasticity and toughness. Key word: 18%Ni cobalt-free maraging steel ultra-high purity melting high isotrope solution treatment ageing strengthening 18%Ni马氏体时效钢是六十年代初由国际镍公司（IN-CO）研制开发的一族新型超高强度钢[1]，该类钢具有超高强度、高韧性、优异的冷加工性能和良好的焊接性能，热处理工艺简单，广泛用于宇航和尖端武器领域[2]。我国从七十年代开始研制马氏体时效钢[3]并且在航空、航天及军工领域得到应用[4][5][6]。 该类钢含有8-12%战略物资钴元素，成本高，价格昂贵，应用受到限制，八十年代国际镍公司（INCO）研制出T250无钴马氏体时效钢[7]，该钢在C250钢基础上去掉钴，降低钼含量，增加了钛含量，由于Mo降低、Ti增加，在相同强度级别与C250钢相比塑韧性会降低，提高钢的塑韧性成为T250钢试制与推广应用的关键，为此进行了超纯净化控制技术、均质化控制技术和钢的热处理工艺及性能的研究，研制T250钢达到C250钢的实物水平[8]，用于制造火箭发动机壳体，使用性能达到C250钢国内现有水平。 T250钢工艺路线 T250钢化学成分见表1 表1 T250马氏体时效钢的化学成分（wet%） ------------------------------------------------------------------------------------------------------- 钢种 C Mn Si S P Ni Co Mo Ti Al T250 ≤ ≤ ≤ ≤ ≤ 18.0 ≤ 2.75 1.2 0.05 0.03 0.10 0.10 0.010 0.010 20.0 0.5 3.25 1.6 0.15 试验钢经VIM熔化，浇注φ520电极，电极磨光后在VAR炉重熔φ610钢锭，钢锭经固溶后车光。钢锭经1250℃高温均质化处理，快锻机开坯，开锻造温度大于1100℃，终锻温度大于800℃；锻坯入加热炉加热，加热温度1050-1150℃，在1300吨液压式精锻机锻造φ220棒材，锻后空冷，钢棒在820--920℃保温4-6小时后空冷。 试验结果 试制钢的化学成分如表2 表2 T250钢的化学成分（wt%） 炉号 C Mn Si S P Ni Co Mo Ti Al 0104 0.01 0.02 0.03 0.002 0.005 19.70 0.16 2.85 1.54 0.12 0105 0.01 0.02 0.05 0.002 0.005 19.70 0.15 2.93 1.50 0.12 2.2 钢的力学性能 试样经820℃×1小时固溶+510℃×3小时时效处理，钢的力学性能如表3 表3 T250钢的力学性能 炉号