冷拉变形量对GH80A合金棒材组织和性能的影.pdfVIP

第15卷第7期 钢铁研究学报 Vol.巧,No. 7 2003年7月 JOURNAL OF IRON AND STEEL RESEARCH July 2003 冷拉变形量对GH80A合金棒材组织和性能的影响 张立红，陈 川，王 华 (宝钢集团上海五钢有限公司研究二所，上海200940) 摘 要:着重研究了冷拉变形量对GH80A合金冷拉棒材晶粒组织和力学性能的影响。结果表明: 随着冷拉变形量的增加，合金的冷拉态硬度不断提高、晶粒组织缓慢变细、瞬时拉伸性能稍有提 高、持久寿命略有下降。合金的冷拉变形量应控制在8%--20%范围内。 关键词GH80A合金;冷拉变形量;硬度;组织;性能 中图分类号:TG132. 3 文献标识码:A 文章编号:1001一0963(2003)07一0430一03 Effect of Cold-Drawn Deformation Amount on Microstructure and Property of Alloy GH80A Bar ZHANG Li-hong, CHEN Chuan, WANG Hua (Baosteel Group Shanghai No. 5 Steel Ltd Co, Shanghai 200940, China) Abstract: The effect of cold-drawn deformation amount on structure and property of GH80A alloy cold 击awn bar has been mainly studied厂rhe results show that with increasing amount of cold-drawn defor- mation, the cold-drawn hardness of alloy can be continuously enhanced, the grain becomes slowly fine, the instantaneous tension test property is increased a little, but the endurance limit is decreased some- what, and the appropriate cold-drawn deformation amount for alloy、be controlled within 8%-20% Key words: GH80A alloy; cold-drawn deformation amount; hardness; structure; property 组织缓慢变细、瞬时拉伸性能稍有提高、持久寿命略 1 前 言 有下降;合金冷拉变形量应控制在8%-20%范围 内。 GH80A合金(英国牌号Nimonic80A)属时效硬 化型镍一铬高温合金，通过添加Al, Ti元素使其强 2 试验用料与试验方法 化。该合金在750℃以下具有较高的强度和良好的 抗氧化性、耐蚀性，并具有良好的冷热加工性能和机 试验用料取自采用真空感应熔炼加电渣重熔， 加工性能[‘」。其冷拉棒材多用作高温紧固件、汽车 经锻造开坯、热轧，再冷拉的GH80A合金棒材，其化 排气阀等重要部件。本文着重研究不同冷拉变形量 学成分、规格及冷拉变形量分别见表1和表2。标准 对GH80A合金冷拉棒材晶粒组织和力学性能的影 热处理制度为1080C x 30min，空冷+7501C X 4h, 响，以