固溶铌对贝氏体相转变动力学的影响.pdfVIP

固溶铌对贝氏体相转变动力学的影响 页码，1/6 固溶铌对贝氏体相转变动力学的影响 G.I.Rees①，J.Perdrix②，T.Maurickx②，H.K.D.H.Bhadeshia① ①英国剑桥大学材料科学与冶金系 ②法国敦克尔克索拉克公司研究开发中心 摘要：采用热膨胀、扫描透射电子显微镜研究了微合金化奥氏体中固溶铌对冷却过程中贝氏 体相转变动力学的影响。所研究的钢为三炉实验室冶炼的不同铌含量的钢和和一种工业生产 的微合金化钢。结果表明，提高铌含量延迟了贝氏体的相转变，但这种影响相当小。冷却前 奥氏体中少量碳氮化铌的析出对贝氏体转变的影响要强烈得多。 关键词：铌；贝氏体 The Effect of Niobium In Solid Solution on The Transformation Kinetics of Bainite Abstract A study in made of the effect of niobium in solid solution in microalloyed sustenite on the kinetics o ftransformation to bainite upon cooling, using a combination of dilatometry, scanning and transmission electron microscopy. The steels investigated are three laboratory melts with systemtic variations jin niobium concentration, and an industrial microalloyed grade. Results indicate that increasing niobium content retards the bainite transforation but that, while significant, this effect is rarther small. A much more dramatic effect on bainite formation is produced by alloying a small amount of niobium carbo-nitride precipitation in the austenite before cooling. Key words: Niobium; Bainite 1.前言 许多作者[1-5]报道过添加铌对钢的淬透性的影响。早期的研究工作大多集中在铌对冷却 过程中非本形铁素体初始形成温度的影响，并指出添加铌抑制了铁素体在奥氏体晶界的形 核，从而减少了铁素体，增加了贝氏体组织。文献 的工作表明，提高奥氏体中固溶 的含 [5] Nb file://C:\Documents and Settings\yhl\桌面\新建文件夹\固溶铌对贝氏体... 2007-5-31 固溶铌对贝氏体相转变动力学的影响 页码，2/6 量显著延迟了非本形铁素体的形成。但是，可观察到延迟效应的最大值，随铌含量超过 一个临界值后，晶界铁素体转变动力学加速。这种情况下，作者们提出冷却过程中碳化铌的 析出领先于铁素体的形成，并作为铁素体加速形核的位置。在这方面，这些结果[3]类似于硼 对铁素体形成的延迟效应，即高的硼含量下，由于铁素体在硼化物质点处的优先形核，硼的 阻碍效应消失。 最近的工作[6]揭示了改变铌微合金化钢中碳化铌析出量对铁素体和贝氏体转变动力学的 影响。最初这些影响被解释为展现了铁素体和贝氏体的形成对冷却奥氏体中固溶铌的敏感程 度。特别是在碳化物溶解量与避免形成除马氏