生产实践 Production Practice A3钢在不同浓度NaHSO3 溶液中的腐蚀动力学研究 金 铎 王国斌 李 楠 任宏瑞 （吕梁学院化学化工系，山西 吕梁 033000 ） 摘 要：利用全浸挂片实验，计算A3钢在不同浓度NaHSO3 溶液中的腐蚀速率和腐蚀深度，得 出其腐蚀动力学规律。结论为：A3钢在三种浓度NaHSO3 溶液中，随着腐蚀时间的增加，腐蚀深度 增加，腐蚀速率呈现减小的趋势，且减小的趋势接近；随着NaHSO3 溶液浓度的增大，初期腐蚀程 度增大。 关键词：A3 NaHSO3 腐蚀深度 腐蚀速率 锈层 中图分类号： 文献标识码： DOI：10.13726/j .cnki.11-2706/tq.2017.04.083.04 TG178 A Research on Corrosion Kinetics of A3 Steel in Different Concentrations of NahSO3 Solution JIN Duo, WANG Guo-bin, LI Nan, REN Hong-rui (Lv Liang University, Lvliang 033000, China) Abstract: The corrosion rate and corrosion depth of A3 steel in different concentrations of NaHSO3 术 技 solution were calculated by using the immersed coupon experiment. The kinetics of corrosion was obtained. The results show that in three concentrations of NaHSO3 solution, as the corrosion cycle increases, the corrosion depth increases and the corrosion rate decreased, and the decreasing trend is close. With the increase of NaHSO3 solution concentration, the initial degree of corrosion increased. Key words: A3; NaHSO ; corrosion depth; corrosion rate; rust layer 3 0 前言 环境中的腐蚀行为做了大量的研究工作，但对其在 A 3钢是一种生活中常见的普通碳素钢，又称 NaHSO3溶液中的腐蚀规律研究较少。因此，本文通 作Q235钢，它的屈服强度为235MPa 。其用途非常 过实验观察A3钢在不同浓度NaHSO3溶液中的腐蚀 广泛，大量应用于建设及工程结构，以及一些对性 现象，计算腐蚀速率及腐蚀深度，得出腐蚀动力学规 能要求不太高的机械零件[1, 2] 。金属腐蚀是指金属材 律，为A3钢在今后的使用过程中提供理论数据基础。 料与所处环境之间相互作用，导致材料变质和破坏 [3] 1 实验 的现象 。对于A3钢所在的环境中