Z18闸板阀盖的铸造工艺和生产.pdfVIP

铸造工程 Foundry Engineering 材料与工艺 Z18闸板阀盖的铸造工艺和生产 贾泽春 （秦皇岛技师学院，河北 秦皇岛， 066000） 摘要：分析了Z18闸板阀盖铸钢件的结构铸造工艺。阐述了该铸钢件的铸造工艺及生产经验， 并针对其箱式结构和耐压的特点，提出了钢芯头定位的新思路。通过采用保温冒口及冒口覆盖 剂加强补缩等工艺措施，有效地防止了铸钢阀盖裂纹和缩松的产生，生产出了合格的铸钢阀 盖，为类似铸钢件的生产提供借鉴。 关键词：阀盖；保温冒口；钢芯头定位；铸造工艺 中图分类号：TG242 文献标识码：B 文章编号：1673-3320（2017）03-0030-04 Casting process and production of Z18 gate valve cap JIA Zechun (Qinhuangdao Technician College, Qinhuangdao 066000, Hebei China) Abstract: The configuration and casting process of steel castings of Z18 gate valve cap were analyzed. The casting technology and production experience for the steel castings were described. A new thinking whereby the steel core head was positioned was put forward on the basis of box construction and resistance to pressure peculiar to the valve cap. The use of such technological measures as insulating riser and covering flux strengthening feeding prevented effectively the steel casting of valve cap from producing crack and shrinkage, and the qualified castings have been produced, thus giving a reference to production of similar steel castings. Key words: valve cap; insulating riser; steel cored head positioning; casting process 阀盖与阀体配套使用，是冶金高炉阀门系统 该阀盖属于箱式结构铸件，壁厚在2 5 ～3 5 中的热风及燃气重要控制部件，其尺寸精度要求 mm 范围。在法兰部位容易产生缩松或缩孔缺陷。 较高，铸件结构尺寸简图如图1所示。Z 18 闸板阀 铸件在收缩过程中会因型、芯阻碍作用产生铸造 盖铸钢件外形尺寸为2 100 mm ×1 800 mm ×650 应力，在两个立脚处易出现裂纹。最大的难题是 mm ，净重2 .7 t ，材质牌号ZG230-450 ，工作压力 舌头芯容易产生漂芯现象，砂芯的定位、排气及 为0 .2 ～0 .3 Mp a 。铸件不允许有裂纹、缩孔、疏 芯铁强度都是待解决的问题，应事先予以重视， 松、气孔、砂眼、夹渣和冷隔等缺陷，须进行0.5 想办法在工艺上予以解决。 Mp a 的水压强度试验，保压30 min 以上不得有渗