核电站重要厂用水系统的腐蚀分析.pdfVIP

专 论 Monograph 核电站重要厂用水系统的腐蚀分析 赵万祥 孔全兴 李伟光 杨宏欢 （苏州热工研究院有限公司，江苏 苏州 215004 ） 摘 要：介绍了国内某核电厂重要厂用水系统(SEC) 的腐蚀环境和面临的腐蚀风险，对系统典 型的腐蚀问题进行分析。说明了防腐设计不合理、运维管理不当是腐蚀产生的根本原因，指出了 完善系统的防腐蚀设计、优化防腐选材、加强运维管理是防止系统腐蚀的有效措施。 关键词：腐蚀 分析 防腐设计 中图分类号： 文献标识码： DOI：10.13726/j .cnki.11-2706/tq.2017.04.011.04 TG172.5 A Corrosion Analysis of Essentail Service Water System for The Nuclear Plant ZHAO Wan-xiang, KONG Quan-xing, LI Wei-guang, YANG Hong-huan (Suzhou Nuclear Power Research Institute, Suzhou 215004, China) Abstract: This paper introduces the corrosion environment and the corrosion risk of essentail service system(SEC) in a nuclear power plant in china. The anticorrosion design is not reasonable, improper operation and maintenance management is the fundamental cause of corrosion, this paper points out that the perfect system of anticorrosive design, optimization of anticorrosion material, strengthen the operation 术 技 and maintenance management system is an effective measure to prevent corrosion. Key words: corrosion; analysis; anti-corrosion design 0 前言 腐蚀事件，对系统安全运行产生了较大影响。本文 滨海核电厂利用海水作为最终冷源来冷却核反 对腐蚀事件进行了详细的原因分析，结合系统防腐 应堆的余热，通过重要厂用水系统 （SEC ）把设备冷 蚀设计及腐蚀运维管理提出改进措施。 却水系统 （RRI ）收集的热负荷输送到海水中，实现 1 腐蚀环境及风险分析 冷却功能。SEC系统为核安全相关系统，按RCCM-3 级标准设计，具有抗震要求。SEC系统主要设备为海 1.1 腐蚀环境 水输送泵、过滤器、相关管道，这些设备都与海水 SEC 系统主要面临海水和海洋大气腐蚀环境。 接触。海水中含有大量的氯离子和其他盐类离子， 海水是含有悬浮泥沙、腐烂微生物、溶解气体、多 是强电解质溶液，具有强腐蚀性。另外，核电厂在 种盐类的复杂强电解质溶液。碳钢和低合金钢阳极 海水入口处添加次氯酸钠来以抑制海生物生长，次 活性高，极化率小，在海水中不能有效钝化，易腐 氯酸钠具有强氧化性，增加了