石英砂 负载氧化铁吸附除磷 fIll研 究 许光眉 施 周 邓 军 (1湖南省建筑设计院，长沙 410011；2湖南大学土木工程学院，长沙 410082) 摘要 通过小试摇床试验研究了石英砂负载氧化铁(IOCS)在不同的试验条件下(pH、吸附时 间、背景离子等)对磷的吸附效果。结果表明：在中性条件下，IOCS吸附除磷效果最佳；锑与磷在 IOCS上产生明显的竞争吸附。准二级反应动力学模型及Langmuir等温吸附模型可分别较好地描 述磷的吸附动力学及吸附等温线试验结果；再生试验表明：采用0．1 mol／L的NaOH溶液可以使得 IOCS再生，且再生次数对吸附容量影响不大。 关键词 负载型氧化铁 磷 吸附 解吸 再生 Study of phosphate adsorption on iron—oxide coated sand Xu Guangmei ，Shi Zhou ，Deng J un2 (J．Architecture Design Institute of Hunan Province，Changsha 410011，China； 2．College of Civil Engineering，Hunan University，Changsha 410082，China) Abstract：Removal of phosphate from aqueous solution using iron—oxide coated sand(IOCS) was investigated by batch experiments under various conditions of pH，adsorption time，and back— ground ions．Experimental results showed that phosphate removal achieved the best at neutral solu— tion，and its competitive adsorption occurred when antimony was added．The data obtained from kinetic and isotherm experiments could be well described using pseudo‘‘second——order rate model and Langmuir isotherm respectively． The regeneration experiments demonstrated that phosphate adsorbed on IOCS can be recovered by 0．1 mol／L NaOH，and times of desorption—regeneration have little effect on the IOCS adsorption capacity． Keywords：Coated iron-oxide；Phosphate；Adsorption；Desorption；Regeneration 0 前言 且不利于磷的回收口]。吸附法除磷效率较高，通过 磷是造成水体富营养化的重要因素，富营养化 再生，吸附剂可以重复利用，为污水深度处理提供一 会造成水体含氧量急剧下降，藻类大量繁殖，增加水 种新的途径。目前常用的吸附剂有：羟基氧化铁口]， 处理的难度和成本。因此废水除磷以及磷的回收是 针铁矿[ ，二氧化钛[引，活性氧化铝[。 ]等，但是此类 近年来水处理研究的一个重点和难点。生物法除磷 吸附剂多为粉末状，虽然比表面积大，有利于磷的吸 效率有限，出水磷含量一般为1 mg／L左右，而且二 附，但是固液分离困难，不利于磷的回收以及吸附剂 沉池有磷的释放，难以完全达到国家污水处理厂排 的再生。 放一级