AlCl3 雾态气体放电下碳钢中低温渗铝 张弋飞1、 2 张昕辉2 1 北京坚润表面材料研究所 北京100034 2 上海领异金属表面材料有限公司 上海200431 摘要：根据三氯化铝 AlCl 化合物物态变化的性质，低压下生成雾态气体 AlCl ；在成雾态气体放电物理及化学作用下， 3 3 10 钢和45 钢在620 ℃温度得到数十μm 渗铝层。 关键词：雾气体放电 渗铝 AlCl3 Low Carbon Steel Aluminizing at Lower Temperature by Mist Gas Discharge 1 2 Zhang Yifei Zhang Xinhui (1、Beijing Tough Lubricating Inst. Beijing 100034) （2、Shanghai Innovation surface Material Co., Ltd Shanghai 200431) Abstract : The mist gas of aluminum chloride (AlCl3) was produced by the pressure and temperature adjustment in vacuum chamber. The mist gas composes chiefly micro/nanometer solid state particles, liquid state particles and pure gas. The novel mist gas discharge generate in the mist gas of low pressure chamber by DC or pulse power, and dozens micron of the aluminizing layer of carbon steels were obtained through physical-chemical reaction under temperature of 620 ℃ Keywords: mist gas discharge Aluminizing AlCl3 渗铝可以提高金属的抗氧化性及耐蚀性，且能增加 理。 离子渗氮的速度及渗氮层的厚度。渗铝方法众多，在 真空容器中有加热装置（8 ）及控制仪表等（9）使 工业上主要应用的方法有两种—固体粉末渗铝和热 容器升温并保持 100℃，即T =100℃ 0 【 】 1 AlCl 放在第二容器（22 ）中， 启动此容器中的加 浸法渗铝法。固体粉末法渗铝在 780℃以上 ，而 3 【 】 2 热浸铝的铝液温度 是 680 ℃至 710℃；也有报道 热装置（23 ）及控制仪表（24 ）使AlCl3 达到并保持 【 】 3 采用辉光等离子体渗铝。 本文介绍一种在真空特定 l20℃。AlCl3 气化进入真空容器致使容器压力加大，