浅议思林电站地下厂房混凝土渗漏水治理工程.doc

浅议思林电站地下厂房混凝土渗漏水治理工程【摘 要】对于水工地下隧洞衬砌施工过程中的情况，裂缝是这一环节极为普遍的问题，主要是受内外温差变化，使其形成各种不同程度的收缩而最终导致了裂缝的形成，尤其是在地下水位较高的隧洞会产生以垂直于水流方向的存在的水压渗水裂缝。裂缝的形成大大影响了建筑的使用性能，因而需要采取相应的措施进行处理。基于此，文章根据思林电站地下厂房混凝土衬砌段局部出现裂缝的处理情况进行探讨。 【关键词】混凝土；施工工艺；化学灌浆；防渗帷幕 On the Thring underground powerhouse concrete seepage water treatment project Zhou Wei-lin (The Thring power plants of the Wujiang Hydropower Development Co., Ltd Sinan Guilin 565100) 【Abstract】Cracks in hydraulic underground tunnel lining construction process, this link is extremely common problem, mainly by the internal and external temperature changes, to form a variety of different degrees of contraction and eventually led to the formation of cracks, especially in groundwaterthe high tunnel will produce hydraulic seepage cracks perpendicular to the direction of flow exists. The formation of cracks greatly affect the performance of the use of the building, and therefore need to take appropriate measures to deal with. Based on this, the article Thring underground powerhouse concrete lining segments processing of local cracks. 【Key words】Concrete;Construction technology;Chemical grouting;Impervious curtain 1. 工程简述 乌江思林水电站位于贵州省思南县境内的乌江上，总装机容量4X250MW，水库正常蓄水位440m，相应库容12.05亿m3，调节库容3.17亿m3，防洪库容1.84亿m3，总库容15.93亿m3，属日周调节水库。本工程为Ⅰ等大（1）型工程，枢纽建筑物由碾压混凝土重力坝、右岸地下引水发电系统、左岸垂直升船机等组成。枢纽工程开发任务以发电为主，其次为航运，兼顾防洪、灌溉等。地下主厂房布置在右岸的山体里，部分结构低于河床高程，从EL349.5m的操作廊道到EL386m的风机室顶拱及边墙混凝土存在渗漏水现象，影响厂房的安全。 表1 S64-1（上游分支管道）主要出水点统计表 表2 S64-2（下游分支管道）主要出水点统计表 2. 思林水电站地下厂房混凝土渗漏危害和原因分析 2.1 危害分析： （1）会使钢筋混凝土内部存在的氢氧化钙溶失，PH值变小，容易导致混凝土结构中的钢筋发生锈蚀，并会加快结构混凝土的碱骨料反应，从而影响到结构安全，缩短了混凝土的使用寿命。 （2）人员和机电设备长期在潮湿的环境中工作、运行，容易发生氡污染，将会影响到身体健康乃至丧失劳动能力，增加设备故障率，减少机电设备的使用寿命若。 （3）影响它表观形象，对思林电站“达标投产”和申报“鲁班奖”的工作带来影响，而且会降低隧道周边围岩的稳定性，危及隧道的结构安全。 2.2 原因分析： 2.2.1 地质情况： 厂房位于大坝右岸的山体内，工程地貌为石灰岩山体且植被茂盛。该地质状况特点为山体孔隙发达，大坝坝基和两岸均为（T1y2）灰岩、白云岩，岩溶系统发育，坝区主要岩溶管道有左岸的K30、K31，右岸S64、Sj2等。S64发育于T1y2-2，Sj2发育于T1y2－3－2层，其间可能受泥质灰岩阻隔，管道之间联系微弱，但均发育于T1y2层中，为同一补给区补给。 2.2.1.1 S64岩溶管道，根据施工开挖揭露情况可分成上、