SY5561标准—摩擦焊钻杆幻灯片.ppt

复验 如果代表一批管子的一个拉伸试样不符合规定要求，制造厂可以从该批中另选三根管子进行复验。若所有复验试样均符合要求，则除将初验时不合格的那根挑出外，该批中的所有管子均应判为合格。若有多于一个的初验试样或至少有一个复验试样不符合规定要求，则制造厂商可选择对该批管子的剩余部分逐根试验，在这种情况下，只需测定不合格项目。复验试样的取样方法见8.1.1.3。由于上述一项或多项判据不合格而拒收的出自同一炉钢的材料，可以进行重新热处理，并作为一批新管子进行复验。 　　　　If the initial tensile test fails to conform to the specified requirements, the manufacturer may elect to test two　additional specimens from the same length and from approximately the same location. If both of the additional　specimens pass, then the lot shall be accepted.　 　　　　If one or both of the additional specimens fail to conform to the requirements, the manufacturer may elect to　test three additional lengths from the same lot. If the specimens from all three lengths conform to the　requirements, then the lot shall be accepted. If one or more of these specimens fail to conform to the　requirement, the lot shall be rejected. Rejected lots may be re-heat-treated and tested as new lots. 8.1.２化学分析 化学分析可采用测定化学成分常用方法中的任意一种，如发射光谱法、X射线法、原子吸收法、燃烧法或湿式分析法。所用的校准方法应能在公认的标准中找到。所有化学分析均应按照ASTM A751进行。 8.1.3纵向冲击试验 方法 　　夏比V型缺口冲击试验温度为21℃±2.8℃（70℉±5℉）。替代的试验温度见SR20（－20℃±2.8℃ ) 。一次试验应包括3个试样。 冲击试样 　　3个试样应平行于管子轴线，径向开槽（见图6）。冲击试样不应从展平的管子上切取。 缺陷试样 　　试样上发现材料缺欠或缺陷时应废弃，不论是断裂前发现还是断裂后发现，可另取一个试样代替它。低于最小吸收能要求的试样不应轻易判为有缺陷试样。 试验频次――第3组（钢级X、G和S） 代表一批管子的3个冲击试样取自一根管子。5?及较小规格管子每200根或更少者为一批，6?规格管予每100根或更少者为一批，每一批管子具有同样的热处理状态，从倍尺长度管子上截取的所有管段只当作一根。 冲击复验――所有组 如果一组冲击试样没有达到7.1.3的要求，制造厂可从同一根管子上再取3个试样复验。3个试样都应达到或超过表11规定的平均最低吸收能要求。 如果复验达不到上述要求，应从该批抽取2根管子各取3个试样，如果从这两根管子上取的复验试样都符合表11的规定，则除原来不合格的那根管子之外该批管子应予以验收。对不合格的管子制造厂可选择重新热处理或重新试验。 If more than one specimen in the initial test is below the minimum specimen absorbed-energy requirement, then the manufacturer may elect either to reject the lot or to re-test an additional set of three specimens from each of three additional pipe bodies from the same lot. If these additional sets of specimens do not meet the initial test requirements, then the lot shall be rejected. 8.1.4尺寸和重量检验 重量检验 每根钻杆