石化装置保温材料的腐蚀性研究 中国石化第五建设有限公司 何贵堂 中国石化扬子石油化工有限公司 章炳华 南京工业大学 魏无际 连洲洋 内容摘要：石化设备由于保温引起的腐蚀泄漏屡有发生，对某石化公司几种常用的保温材料可溶性组分进行提取，并对其腐蚀性成分进行分析研究。认为海泡石硅酸盐的SO42-、Cl-含量最高，腐蚀性最大，应慎用；复合硅酸盐（Cl-+F-）离子含量Study on the Corrosion of Thermal Insulation Material for Petrochemical Device The Fifth Construction Company of Sinopec He Guitang Sinopec Yangzi Petrochemical Company Ltd. Zhang Binghua Nanjing University of Technology Wei Wuji Lian Zhouyang Abstract：Due to insulation, corrosion leakage of petrochemical device occured frequently. Soluble components of several commonly used thermal insulation materials were extracted, and the corrosive components were analyzed. Sepiolite, composite silicate and superfine glass wool should be used with caution because of the serious corrosion due to high electrical conductivity and high content of SO42- and Cl-. The ion contents (Cl-+F-) of composite silicate and superfine glass wool were the highest, but the ion contents of aluminum silicate fiber was the lowest which was suitable for the austenitic stainless steel device as thermal insulation material. Keywords: Petrochemical device Thermal insulation material Corrosive components Analysis 1 引言 国内保温材料在石化行业中已大量使用，对设备管道由于保温材料引起的腐蚀泄漏屡有发生，一方面是因为保温材料具有很大的表面积和丰富的毛细管，具有很强的吸水能力，一旦保温层结构不完善或损坏，导致雨水侵入，使设备金属表面形成水膜而腐蚀；另一方面，保温材料大多是由矿物质加工而成，保温材料中含有腐蚀性介质，加速了水对金属表面的均匀腐蚀。特别是保温材料中含有的或在使用中侵入的氯化物、氟化物及硫化物等腐蚀性成分不仅加速了均匀腐蚀，也会引起局部腐蚀，乃至应力腐蚀开裂(SCC)。目前，国内对保温材料的腐蚀性成分研究较少。 对某石化公司几种常用的保温材料可溶性组分进行提取，并对腐蚀性成分进行分析研究。 2实验部分 2.1 实验仪器 表1 实验所用仪器 仪器名称 数量 生产厂家 电导率测定仪 一台 紫外分光光度计() 一台 上海电化学工作站(CHI660B) 一台 上海辰华电子仪器有限公司 图1 提取时间和氯离子含量关系 2.4 测定 按照试验测定标准JC／T 618—2005《绝热材料中可溶出的氯化物、氟化物、硅酸盐及钠离子的化学分析方法》，对几种保温材料中的电导率、 pH值和硫酸根、氯、氟、钠、硅酸根等进行测定。 3 测定结果与讨论分析 3.1 各种新旧保温材料提取液的电导率 各种新旧保温材料提取液的电导率、pH值和SO32-、CL-等的测定值汇总见表3。（表3把测定的原几组图表数据汇总） 表3 10种新旧保温材料提取液所对应的电导率、pH值和SO32-、CL-测定值汇总表 保温材料 旧岩棉 新岩棉 旧矿渣棉 旧超细玻璃棉 新超细玻璃棉 旧复合硅酸盐 新复合硅酸盐 旧硅酸铝 新硅酸铝 旧膨胀珍珠岩 旧海泡石 旧微孔硅酸钙 旧泡沫玻璃 旧聚氨酯 电导率（μS/cm） 90 67.3 93 148 95.9 167.1 135.3 53.4 45.5 182.3 8