　～综 　　述～ 我国齿轮热处理技术概况及发展趋势 阎承沛 (北京机电研究所 ,北京 100083) 摘 　要 : 本文论述了我国齿轮热处理技术的现状 ,重点阐述了齿轮受力状况及技术要求 ,齿轮 材料与加工形成 ,齿轮热处理工艺研究进展 ,齿轮热处理缺陷及技术改进 ,齿轮热处 理新工艺技术开发以及齿轮热处理设备的研制与开发等 。同时 ,对我国齿轮热处理 技术的发展趋势进行了初步探讨 。 关键词 : 齿轮热处理 ;概况 ;发展趋势 中图分类号 :TG162. 73 　文献标识码 :B　文章编号 :1008 - 1690( 2002) 01 - 0014 - 11 General Situation and Progress Tendency for Gear Heat Treatment Technology in China YAN 　Cheng - pei (Beijin g Research Institute of Mechanical Electrical Technology ,Beijin g 100083 ,China) Abstract :The paper dealed with general Situation of gear heat treatment technology in China. It is introduced primarily forced situation analyses and specification , gear material and formed ,research and development of gear heat treatment processing ,gear heat treatment defects and technical inno valion ,gear heat treatment new processing development as well as gear heat treatment equipment development et al in China. Simultaneously ,it is inquired preliminary into gear heat treatment tech nolo gy pro gress tendency in China. Key words :gear heat treatment ;general situation ;pro gress tendency 1 　概况 式为弯曲疲劳破坏[ 1 ] 。 1. 1 　齿轮受力状况及技术要求 通过齿轮破坏形式的分析研究 ,可以看 众所周知 ,齿轮是机械设备中的重要零 出 ,齿轮要求具有优良的耐磨性 、抗接触疲劳 件 ,齿轮在传递力及改变速度的运动过程中 , 和抗弯曲疲劳性能 。也就是说 ,齿轮表面硬 啮合齿面之间既有滚动 ,又有滑动 ,而且齿面 度高 、强度高 、心部韧性好 ,硬化层分布合理 。 还受到脉动或交变弯曲应力的作用 。即下面 1. 2 　齿轮材料与加工成形 三种形式 : 1. 2. 1 实践证明,一般机床齿轮选用中碳钢制 1. 1. 1 啮合齿面间的摩擦力及齿面磨损 ,破坏 造 ,并经感应加热表面淬火处理 ,所得到的硬 形式为氧化磨损 ,冷咬合磨损和热咬合磨损 。 度 、耐磨性、强度及韧性均能满足要求 ,而且感 1. 1. 2 啮合齿面的接触应力及接触疲劳 ,破 应加热表面淬火件具有不易氧化 、脱碳和变形 坏形式有表面麻点 ,浅层剥落及涂层剥落