混凝土抗硫酸盐侵蚀实验的研究 XX 指导老师：XXX 摘要：本文采用沉淀滴定法测定在相同水胶比（0.4）的条件下，不同配比的混凝土浸泡在不同浓度的硫酸盐（离子浓度1000 mg/l、4000 mg/l、10000mg/l、20250 mg/l）所受到的侵蚀情况不同，根据消耗氯化钡的量，从而计算出由不同比例单复掺Ⅱ级粉煤灰、矿渣和不同掺量的粉煤灰、矿渣混合而成的混凝土在不同龄期（28d、60d、120d、180d）的抗硫酸盐侵蚀能力，从该实验中可知混凝土的抗侵蚀能力和粉煤灰、矿渣掺量的有关，掺量大则抗侵蚀能力强。 关键词：硫酸盐；侵蚀；混凝土 Study on the concrete sulphate erosion Xx Xxx Tutor :Xx Xxx Abstract: This article is written by titration method to determine the water spray（0.4） is in the same conditions, different proportion concrete in different levels of sulphate（1000 mg/l、4000 mg/l、10000mg/l、20250 mg/l） had been the erosion of the situation is different, according to the quantity of consumption barium chloride, thus calculated in proportion to the back with a grade ii flyash and a quantity of flyash a mixture of concrete not the same age（28d、60d、120d、180d） issue of resisting sulphate on the ability. From the experiment the ability that erosion resistance of concrete admixture of fly ash and slag, the relevant, while the admixture of big erosion resistance ability. Keywords: Sulphate；Erosion；Concrete ，多年来，国内外许多学者在侵蚀机理方面，并得到了一些结论。但由于，到目前为止仍没有一种研究方法能快速，有时由于，得到的结论也会有所，甚至相互矛盾符合国家标准GB/T17671《水泥胶砂强度检验方法(ISO法)》要求的在中国境内生产、销售、使用的标准砂mg/l;3)硫酸根离子浓度4000mg/l;4)硫酸根离子浓度10000mg/l;5)硫酸根离子浓度20250mg/l;五种不同浓度的硫酸根离子浓度的溶液中。通过硫酸盐侵蚀实验，测试不同试件在不同溶液中浸泡不同时间的抗折强度，计算抗折系数，分析高性能混凝土在水胶比相同，不同掺合料掺量，不同侵蚀龄期的情况下对混凝土抗侵蚀性能的影响。 水泥抗硫酸盐侵蚀标准试验方法国内有GB749-65慢蚀法和GB2420-81快速法两种，本实验宏观方法是参照GB/749-2008《水泥抗硫酸盐侵蚀试验方法》中的“浸泡抗蚀性能试验方法（K）”[7] 。通过侵蚀实验，研究混凝土中砂浆因侵蚀而发生的力学性质变化和侵蚀破坏现象。 本试验采用10mm×10mm×60mm的胶砂试件，以抗折系数作为判定指标，进行抗硫酸盐侵蚀实验。其中抗蚀系数按如下公式进行计算： K=f侵蚀溶液/f淡水 式中：f侵蚀溶液—砂浆试件浸泡在侵蚀溶液中到规定龄期的抗折强度（MPa）； f淡水 ——砂浆试件浸泡在淡水中与侵蚀溶液中试件同龄期的抗折强度（MPa）； K—胶砂试件抗蚀系数。 评价试件抗硫酸盐侵蚀能力的强弱，以抗蚀系数K≥0.8为抗蚀合格，K＜0.8为抗蚀不合格，即认为试件被侵蚀破坏了。 3 实验结果及结果的处理 对相同水胶比、不同掺合料掺量、不同龄期的胶砂试件的抗折强度、抗蚀 数进行测定，测定结果见附表1。 在相同水胶比的情况下，养护3天后，浸泡在浓度为1000mg/l硫酸根离子中，各组试件抗侵蚀系数随龄期变化而变化的关系曲线如下： 注：图3-1 A1：粉煤灰掺量30% A2：粉煤灰掺量50% A3：矿渣微粉掺量30% A4：矿渣微粉掺量50% 注：图3-2 A5：粉煤灰掺量22.5%，矿渣微粉掺量7.5% A6：粉煤灰掺量10%，矿渣微粉掺量20% A7：粉煤灰掺量15%，矿渣微粉掺量15% 注：图3-