铸钢冷却壁铸造工艺.pdf

学兔兔 Apr．2011 · 404· V0I．60 N0．4 铸钢冷却壁的铸造工艺 李 平 (武汉钢铁重工集团，湖北武汉430083) 摘要：铸钢冷却壁作为换代高炉冷却壁，它与铸铁冷却壁相比有着本质上的性能提升。介绍了铸钢冷却壁铸造过程中 各工序的要点，并针对冷却壁热面砖槽造型、冷却水管防熔穿措施和浇注过程控制等铸造难点给出了多种工艺方案， 并通过生产实践证明了工艺方案的可行性。 关键词：铸钢冷却壁；铸造工艺；高炉冷却设备 中图分类号：TG269 文献标识码：B 文章编号：1001—4977(2011)04—0404—03 Foundry TechniqFound echnique ot ast tee of Cast SteeI Cooling StaveI ooling tave LI Ping (WISCO Heavy Industries，Wuhan 430083，Hubei，China) Abstract：As an updated cooling stave for blast furnace，the steeI cooling stave has essentiaI performance improvements compared with the iron cooling stave．The key points of each process steps in casting of steeI cooling stave were presented and multiple solutions were given to the foundry difficulties such as brick trench’S moulding．cooling pipes’meltdown-proof measures and pouring process contro1．These solutions are proved to be feasible through the successfuI manufacture． Key words：cast steel cooling stave；foundry technique；furnace cooling equipment 与铸铁冷却壁相比，铸钢冷却壁具有导热性高、 冷却壁本体选用20％o的缩尺，冷却水管选用18％o的缩 抗热冲击性能好等优点，更适应高炉炉内的工况条件， 尺，然后根据试制结果及时修正各种参数。 但同时也存在着易粘砂、尺寸不易保证、冷却水管易 1。2 砖槽部位的模样设计 被熔穿等问题。本厂早在2000年左右就开始了铸钢冷 冷却壁热面镶耐火砖用的砖槽部位是铸造难点之 却壁的研制[1]，在十多年的不断摸索中，已经形成了一 一 ， 砖槽部位的砂型造型方法一般有两种。第一种是 整套成熟的铸造工艺，能够保证浇注过程中冷却壁内 将砖槽部位的齿状砂型设计成砂芯，通过下芯的方式 的冷却水管 “熔而不穿”且能够通过通球、水压试验， 来形成砖槽型腔，如图1。但是该方法有以下缺点：大 冷却壁本体光洁、尺寸精确。下面